Multicomponent Polymer Systems: Phase Behavior, Dynamics and Applications : November 29-December 3, 2004, Boston, Massachusetts, USA. |
From inside the book
Results 1-3 of 9
Page 38
... PMMA , although the UV polymerized PMMA gives a higher fluorescence background , possibly due to the presence of monomer and other impurities in the samples . UV Polymerized Melt - blended 1000 2000 Raman Shift ( cm1 ) 3000 4000 Figure ...
... PMMA , although the UV polymerized PMMA gives a higher fluorescence background , possibly due to the presence of monomer and other impurities in the samples . UV Polymerized Melt - blended 1000 2000 Raman Shift ( cm1 ) 3000 4000 Figure ...
Page 39
... PMMA backbone shown in Fig . 3a , the sidechain symmetry is hindered by isotropic SWNT / PMMA interactions shown in Fig . 3b . Since the side chain vibrations are sensitive to the tangential orientation of PMMA / SWNT interaction , the ...
... PMMA backbone shown in Fig . 3a , the sidechain symmetry is hindered by isotropic SWNT / PMMA interactions shown in Fig . 3b . Since the side chain vibrations are sensitive to the tangential orientation of PMMA / SWNT interaction , the ...
Page 41
... PMMA Tg temperature in the composite , further enhances anisotropic interaction over random diffusion by the differential expansion / contraction effect from PMMA / SWNT . This interfacial interaction affects conformations of both PMMA ...
... PMMA Tg temperature in the composite , further enhances anisotropic interaction over random diffusion by the differential expansion / contraction effect from PMMA / SWNT . This interfacial interaction affects conformations of both PMMA ...
Contents
Rich Dynamics in Diblock Copolymers | 1 |
On the Origin of Color Degradation in Polyfluorenes Block Copolymer | 14 |
Influence of the Particle Morphology on the MicroAnd Macromechanics | 30 |
Copyright | |
2 other sections not shown
Common terms and phrases
2005 Materials Research amorphous annealing behavior block copolymers chain Chem cluster co-continuous component composite electrodes conductivity counterion crystalline decrease diffusion dynamic mechanical analysis dynamics E-MA-GMA effect emission endothermic epoxide ESC resistance experimental extruded fiber length fibrous clay filler films flexural modulus fluid glass transition glass transition temperature HDPE homopolymer Im3m immiscible increases initiator intensity interactions interfacial ionomer irradiated layer liquid crystal Macromolecules Materials Research Society matrix measurements mechanical properties melt melt-blended composite membranes molecular weight monomers morphology Nafion nanocomposites nanoparticles nanorods NTDA-ODADS/ODA observed obtained P(VDF-TrFE parameters particles PCLD peak performance PFOS phase separation Phys platelet PMDA PMMA polarization polydisperse polyimide polyimide copolymers polymer blends polymerization polystyrene pore PS/PP Raman ratio room temperature samples SAXS shown in Figure shows simulation solvent spectra spheres strain structure surface SWNT TFPS(II TFPSF thermal volume fraction X-ray