Multicomponent Polymer Systems: Phase Behavior, Dynamics and Applications : November 29-December 3, 2004, Boston, Massachusetts, USA. |
From inside the book
Results 1-3 of 18
Page 44
... relaxation , y , at approximately -190 ° C was attributed to motions of the SO2F group . The ẞ relaxation was found to be a broad peak in the range from -100 to -20 ° C . At low frequencies , this peak could be resolved into two ...
... relaxation , y , at approximately -190 ° C was attributed to motions of the SO2F group . The ẞ relaxation was found to be a broad peak in the range from -100 to -20 ° C . At low frequencies , this peak could be resolved into two ...
Page 52
... relaxation in the DMA correlates very well with the drop in intensity of the ionomer peak and that the temperature at which this occurs is strongly dependent on the strength of the electrostatic network , which is established by the ...
... relaxation in the DMA correlates very well with the drop in intensity of the ionomer peak and that the temperature at which this occurs is strongly dependent on the strength of the electrostatic network , which is established by the ...
Page 53
... relaxation is greatly affected by the counterion and transitions in backbone dynamics ( NMR ) have been observed at temperatures around the ẞ relaxation lead to the conclusion that this relaxation in due to motions of both the side- and ...
... relaxation is greatly affected by the counterion and transitions in backbone dynamics ( NMR ) have been observed at temperatures around the ẞ relaxation lead to the conclusion that this relaxation in due to motions of both the side- and ...
Contents
Rich Dynamics in Diblock Copolymers | 1 |
On the Origin of Color Degradation in Polyfluorenes Block Copolymer | 14 |
Influence of the Particle Morphology on the MicroAnd Macromechanics | 30 |
Copyright | |
2 other sections not shown
Common terms and phrases
2005 Materials Research amorphous annealing behavior block copolymers chain Chem cluster co-continuous component composite electrodes conductivity counterion crystalline decrease diffusion dynamic mechanical analysis dynamics E-MA-GMA effect emission endothermic epoxide ESC resistance experimental extruded fiber length fibrous clay filler films flexural modulus fluid glass transition glass transition temperature HDPE homopolymer Im3m immiscible increases initiator intensity interactions interfacial ionomer irradiated layer liquid crystal Macromolecules Materials Research Society matrix measurements mechanical properties melt melt-blended composite membranes molecular weight monomers morphology Nafion nanocomposites nanoparticles nanorods NTDA-ODADS/ODA observed obtained P(VDF-TrFE parameters particles PCLD peak performance PFOS phase separation Phys platelet PMDA PMMA polarization polydisperse polyimide polyimide copolymers polymer blends polymerization polystyrene pore PS/PP Raman ratio room temperature samples SAXS shown in Figure shows simulation solvent spectra spheres strain structure surface SWNT TFPS(II TFPSF thermal volume fraction X-ray