Materials Selection for Process Plants |
From inside the book
Results 1-3 of 65
Page 62
... grades of pearlitic malleable iron are covered by ASTM specifica- tion A - 220 . An analysis of malleable iron is ... grades to 90,000 psi for the pearlitic grades . As the tensile strength increases , the elongation decreases . The in ...
... grades of pearlitic malleable iron are covered by ASTM specifica- tion A - 220 . An analysis of malleable iron is ... grades to 90,000 psi for the pearlitic grades . As the tensile strength increases , the elongation decreases . The in ...
Page 64
... grades of nodular iron . Grade 60-45-10 ( ferritic ) and Grade 80-60-03 ( pearlitic ) are general - purpose irons cov- ered in ASTM A - 339 . Pressure - vessel grade nodular irons for service at elevated temperature are specified as ...
... grades of nodular iron . Grade 60-45-10 ( ferritic ) and Grade 80-60-03 ( pearlitic ) are general - purpose irons cov- ered in ASTM A - 339 . Pressure - vessel grade nodular irons for service at elevated temperature are specified as ...
Page 89
... grades . The danger of cracking due to air - hardening is eliminated in the ferritic grades . Cold - working is also easily performed ; work - harden- ing is minimized . Ferritic steels , when heated to about 200-300 ° F , are more ...
... grades . The danger of cracking due to air - hardening is eliminated in the ferritic grades . Cold - working is also easily performed ; work - harden- ing is minimized . Ferritic steels , when heated to about 200-300 ° F , are more ...
Contents
FANSTEEL METALLURGICAL CORPORA | 1 |
HERCULES POWDER COMPANY | 8 |
JESSOP STEEL COMPANY | 16 |
Copyright | |
28 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum aluminum alloys amounts annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride coat cold-working combination common composition compounds concentrations conductivity construction containing continuous cooling copper corrosion resistance cracking ductility effect electrical elevated Elongation environments equipment excellent expansion fabrication given grades gray greater handled hardness heat heat-treatment improved increase industries lead less limited lower machining material maximum mechanical properties metal method Monel nickel nitric normally occurs operating organic oxidizing paint performed physical pipe pitting plastic prevent produced protection range readily recommended reducing removed rubber salts severe silicon solutions solvents stainless steels strength psi stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal tion titanium Type Typical welding widely wrought zinc