Mechanical MetallurgyI Mechanical Fundamentals 1 Introduction 2 Stress and Strain Relationships for Elastic Behavior 3 Elements of the Theory of Plasticity II Metallurgical Fundamentals 4 Plastic Deformation of Single Crystals 5 Dislocation Theory 6 Strengthening Mechanisms 7 Fracture III Applications to Materials Testing 8 The Tension Test 9 The Hardness Test 10 The Torsion Test 11 Fracture Mechanics 12 Fatigue of Metals 13 Creep and Stress Rupture 14 Brittle Fracture and Impact Testing IV Plastic Forming of Metals 15 Fundamentals of Metalworking 16 Forging 17 Rolling of Metals 18 Extrusion 19 Drawing of Rods, Wires and Tubes 20 Sheet-Metal Forming 21 Maching of Metals Appendixes |
From inside the book
Results 1-3 of 33
Page 524
... hot - working and cold - working operations . Hot - working is defined as deformation under conditions of tempera- ture and strain rate such that recovery processes take place simultaneously with the deformation . On the other hand ...
... hot - working and cold - working operations . Hot - working is defined as deformation under conditions of tempera- ture and strain rate such that recovery processes take place simultaneously with the deformation . On the other hand ...
Page 525
... hot - working , unless the effects of cold - work are relieved by annealing . It is important to realize that the distinction between cold - working and hot - working does not depend on any arbitrary temperature of deformation . For ...
... hot - working , unless the effects of cold - work are relieved by annealing . It is important to realize that the distinction between cold - working and hot - working does not depend on any arbitrary temperature of deformation . For ...
Page 527
... hot - working is large ( e≈ 2 to 4 ) compared with tension or ( ɛ creep tests . Hot - working usually is carried out at temperatures above 0.67 , and at high strain rates in the range 0.5 to 500 s1 . The hot torsion test ( Sec . 10-6 ) ...
... hot - working is large ( e≈ 2 to 4 ) compared with tension or ( ɛ creep tests . Hot - working usually is carried out at temperatures above 0.67 , and at high strain rates in the range 0.5 to 500 s1 . The hot torsion test ( Sec . 10-6 ) ...
Contents
Introduction | 3 |
Stress and Strain Relationships for Elastic Behavior | 18 |
Metallurgical Fundamentals | 101 |
Copyright | |
16 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum angle annealed ASME ASTM atoms axis behavior billet brittle fracture Burgers vector cold-worked components compression constant crack creep cycles decrease determined diameter direction dislocation line ductile edge dislocation elastic elongation embrittlement energy engineering equation extrusion factor failure fatigue limit fibers Figure flow curve flow stress force forging friction given grain boundaries hot-working hydrostatic increase indentation lattice length load machining martensite material matrix maximum measured mechanical metallurgical Metals Park modulus necking notch occurs particles percent plane-strain plastic deformation plastic strain pressure produce properties ratio recrystallization reduction region residual stresses rolling screw dislocation shear stress sheet shown in Fig slip plane slip systems Society for Metals specimen steel strain hardening strain rate stress-strain curve structure surface temperature tensile strength tensile stress tensor thickness tool torsion Trans usually velocity workpiece yield strength yield stress