Handbook of Silicone Rubber Fabrication |
From inside the book
Results 1-3 of 14
Page xxviii
... modulus , which in rubber parlance is the stress required to produce a particular elongation . It is a measure of the material's stiffness . It is not a constant and therefore is not the same as Young's modulus for rigid materials . It ...
... modulus , which in rubber parlance is the stress required to produce a particular elongation . It is a measure of the material's stiffness . It is not a constant and therefore is not the same as Young's modulus for rigid materials . It ...
Page 39
Wilfred Lynch. ( shear modulus ) of the specimen . As the modulus increases during vulcanization , torque is recorded against time , to give a cure curve of modulus against time . The Rheograph modulus time chart provides a direct method ...
Wilfred Lynch. ( shear modulus ) of the specimen . As the modulus increases during vulcanization , torque is recorded against time , to give a cure curve of modulus against time . The Rheograph modulus time chart provides a direct method ...
Page 88
... modulus stocks . It may not work at all with low durometer , low modulus stocks , especially PMQ types . It is a preferred method for large moldings or moldings with compli- cated contours at the parting line . Sometimes tear trimming ...
... modulus stocks . It may not work at all with low durometer , low modulus stocks , especially PMQ types . It is a preferred method for large moldings or moldings with compli- cated contours at the parting line . Sometimes tear trimming ...
Contents
THE UNIQUE PROPERTIES OF SILICONE RUBBER | 1 |
THE COMPOUNDING OF HEAT VULCANIZING | 23 |
THE MOLDING OF HEAT VULCANIZING SILICONE | 43 |
Copyright | |
9 other sections not shown
Common terms and phrases
adhesive applied ASTM automatic benzoyl peroxide bonded cable calender catalyst catheter cavity CH3 CH3 CH3 Chemical clamp clean coating compression molding compression set conductor core cycle diameter Dielectric Constant Dielectric strength dispersion Dow Corning durometer elastomer electrical electrical insulating Elongation Engineering equipment extruded fabric fillers flash flexibility flow Foley Catheter FVMQ gaskets glass heat high temperature hydraulic illustrated in Fig implant inflatable seals injection molding insert kg/cm² liquid machine mandrel material metal method mill modulus moisture mold temperature operator organic rubbers oven peroxide pins plastic plate polymer post curing postcure preform pressure properties reinforced removed resistance Rheometer roll runner system screw shaft sheet silica silicone fluids silicone rubber silicone rubber compound silicone rubber insulation siloxane solvent sponge sprue station steel stocks surface tape Tensile strength thickness thin tion transfer molding tubing vinyl volume vulcanization wire