Engineering Materials and Their ApplicationsThis edition of the classic text/reference book has been updated and revised to provide balanced coverage of metals, ceramics, polymers and composites. The first five chapters assess the different structures of metals, ceramics and polymers and how stress and temperature affect them. Demonstrates how to optimize a material's structure by using equilibrium data (phase diagrams) and nonequilibrium conditions, especially precipitation hardening. Discusses the structures, characteristics and applications of the important materials in each field. Considers topics common to all materials--corrosion and oxidation, failure analysis, processing of electrical and magnetic materials, materials selection and specification. Contains special chapters on advanced and large volume engineering materials plus abundant examples and problems. |
From inside the book
Results 1-3 of 35
Page 273
... residual stress of 30,000 psi ( 207 MPa ) . If the dials on the machine were covered , how could we determine the residual stress ? We could inscribe two marks very accurately , 1 in . apart on the gage length , and then make a saw cut ...
... residual stress of 30,000 psi ( 207 MPa ) . If the dials on the machine were covered , how could we determine the residual stress ? We could inscribe two marks very accurately , 1 in . apart on the gage length , and then make a saw cut ...
Page 274
... residual tension ; the resistance increases with residual compression . The precision of the method is excellent , because 1 μohm change is equiva- lent to about 0.000001 in./in . strain , or a residual stress ... residual stresses are ...
... residual tension ; the resistance increases with residual compression . The precision of the method is excellent , because 1 μohm change is equiva- lent to about 0.000001 in./in . strain , or a residual stress ... residual stresses are ...
Page 307
... residual flux pre- sent on the weld surface . Although hand peening may be used , shot blasting can produce more uniform cleaning and stress removal . A residual stress in compression that is developed by peening may even be an ...
... residual flux pre- sent on the weld surface . Although hand peening may be used , shot blasting can produce more uniform cleaning and stress removal . A residual stress in compression that is developed by peening may even be an ...
Contents
Fundamentals | 1 |
Effects of Temperature on Structure and Mechanical | 3 |
CORROSION OF CERAMICS AND PLASTICS S38 | 38 |
Copyright | |
38 other sections not shown
Other editions - View all
Engineering Materials and Their Applications Richard Aloysius Flinn,Paul K. Trojan Snippet view - 1990 |
Common terms and phrases
alloy aluminum annealed applied atoms austenite bainite bond brittle Calculate carbide carbon cast iron cathode cement ceramics Chapter chemical cold-worked components composition compressive concrete cooling copper corrosion crack crystal crystalline curve deformation density developed diffusion discussed ductility effect elastic electrical electron hole electrons elements elongation energy engineering equilibrium ES/E ES/EJ example ferrite fibers fracture toughness glass grain boundaries graphite hardening hardness heat higher important ions layer liquid load magnetic martensite material matrix mechanical melting metal microstructure modulus mold molecules monomer nickel obtain occurs oxide particles pearlite percent percentage phase diagram plane plastic polymer polymerization produce properties quenched ratio reaction resistance Sections shown in Figure shows shrinkage silica silicon sintering solid solution specimen strain structure surface Table tensile strength thermal thermoplastic thermosetting tion transformation ture unit cell weld yield strength zinc