Proceedings of the 10th International Conference on Offshore Mechanics and Arctic Engineering, 1991: Presented at the 10th International Conference on Offshore Mechanics and Arctic Engineering, Stavanger, Norway, June 23-28, 1991. Materials engineering, Volume 3Mamdouh M. Salama American Society of Mechanical Engineers, 1991 - 323 pages |
From inside the book
Results 1-3 of 85
Page 343
... compared with S - N curves for joints with t / T 1 : 45 ° welds . Fig . 4b Total lives of joints with constant t = 26 mm compared with S - N curves for joints with t / T = 1 : 45 ° welds . Attachment Thickness and Weld Profile ...
... compared with S - N curves for joints with t / T 1 : 45 ° welds . Fig . 4b Total lives of joints with constant t = 26 mm compared with S - N curves for joints with t / T = 1 : 45 ° welds . Attachment Thickness and Weld Profile ...
Page 388
... compared with constant amplitude lives measured on identical T- joints in the previous program in S - N diagrams shown in Figs . 4 ( a and b ) . The variable amplitude results are represented by the root mean square stress and the ...
... compared with constant amplitude lives measured on identical T- joints in the previous program in S - N diagrams shown in Figs . 4 ( a and b ) . The variable amplitude results are represented by the root mean square stress and the ...
Page 470
... compared with published finite element results from references 1 and 2 . Results for an X - joint subjected to axial load are tabulated in Table 1. It can be seen from the results that FACTS predictions are between 3 % and 27 % higher ...
... compared with published finite element results from references 1 and 2 . Results for an X - joint subjected to axial load are tabulated in Table 1. It can be seen from the results that FACTS predictions are between 3 % and 27 % higher ...
Contents
THICKNESS EFFECT | 305 |
OFFSHORE TECHNOLOGY PART | 315 |
Influence of the Welding Procedure on the Ferrite Content and Fracture Toughness of Duplex | 323 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
A36 steel as-welded joints assessment Basic behaviour bending brace calculated cathodic protection chord comparison composite computed corrosion fatigue crack depth crack front crack growth rate crack initiation crack length crack propagation crack tip cruciform joints defect diameter Dover failure fatigue crack growth fatigue life predictions fatigue strength fatigue test Figure finite element finite element analysis fracture mechanics geometry impact improved increasing integration layer method Nominal Stress number of cycles Offshore Mechanics offshore structures OMAE parameters parametric equations performed plastic plate thickness procedure ratio residual stress root S-N curves saddle seawater short cracks shown SIF solutions specimens strain strain gauge strand stress concentration stress concentration factors stress distribution stress intensity factor stress range surface crack T-joints Table technique Tee joints temperature tendon tensile tension tubular joints values variable amplitude Volume III-B weight function weld profile weld toe Welded Joints weldments wire