Proceedings of the 10th International Conference on Offshore Mechanics and Arctic Engineering, 1991: Presented at the 10th International Conference on Offshore Mechanics and Arctic Engineering, Stavanger, Norway, June 23-28, 1991. Materials engineering, Volume 3Mamdouh M. Salama American Society of Mechanical Engineers, 1991 - 323 pages |
From inside the book
Results 1-3 of 85
Page 305
... thickness effect of fatigue strength was investigated on welded steel joints with thicknesses ranging from 10 to 80mm . As - welded cruciform joints and Tee joints were tested under pulsating tension and pulsating bending , respectively ...
... thickness effect of fatigue strength was investigated on welded steel joints with thicknesses ranging from 10 to 80mm . As - welded cruciform joints and Tee joints were tested under pulsating tension and pulsating bending , respectively ...
Page 315
... thickness effect backed by a reasonable criterion are required for fabricating structures with heavy section plates . In this study , the thickness effect was investigated by systematic experiments on welded steel joints with thicknesses ...
... thickness effect backed by a reasonable criterion are required for fabricating structures with heavy section plates . In this study , the thickness effect was investigated by systematic experiments on welded steel joints with thicknesses ...
Page 318
... THICKNESS EFFECT CRITERION It was revealed that thickness effect depends not only on the types of joints and loading modes but also on the fatigue lives to be evaluated . Direct application of these results , however , is impractical ...
... THICKNESS EFFECT CRITERION It was revealed that thickness effect depends not only on the types of joints and loading modes but also on the fatigue lives to be evaluated . Direct application of these results , however , is impractical ...
Contents
THICKNESS EFFECT | 305 |
OFFSHORE TECHNOLOGY PART | 315 |
Influence of the Welding Procedure on the Ferrite Content and Fracture Toughness of Duplex | 323 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
A36 steel as-welded joints assessment Basic behaviour bending brace calculated cathodic protection chord comparison composite computed corrosion fatigue crack depth crack front crack growth rate crack initiation crack length crack propagation crack tip cruciform joints defect diameter Dover failure fatigue crack growth fatigue life predictions fatigue strength fatigue test Figure finite element finite element analysis fracture mechanics geometry impact improved increasing integration layer method Nominal Stress number of cycles Offshore Mechanics offshore structures OMAE parameters parametric equations performed plastic plate thickness procedure ratio residual stress root S-N curves saddle seawater short cracks shown SIF solutions specimens strain strain gauge strand stress concentration stress concentration factors stress distribution stress intensity factor stress range surface crack T-joints Table technique Tee joints temperature tendon tensile tension tubular joints values variable amplitude Volume III-B weight function weld profile weld toe Welded Joints weldments wire