Proceedings of the 10th International Conference on Offshore Mechanics and Arctic Engineering, 1991: Presented at the 10th International Conference on Offshore Mechanics and Arctic Engineering, Stavanger, Norway, June 23-28, 1991. Materials engineering, Volume 3Mamdouh M. Salama American Society of Mechanical Engineers, 1991 - 323 pages |
From inside the book
Results 1-3 of 73
Page 340
... toe pass may to Corrected by light grinding Fig . 2c AWS weld profile on instrumented joint with t / T 102/102 mm . = Note Minimum requirements for outside weld at tubular connections designated to ... Weld- Joint No./ Weld profile t /. 340.
... toe pass may to Corrected by light grinding Fig . 2c AWS weld profile on instrumented joint with t / T 102/102 mm . = Note Minimum requirements for outside weld at tubular connections designated to ... Weld- Joint No./ Weld profile t /. 340.
Page 344
... welds . == Effect of Weld Profile Stress Range - 150 MPa served in several joints , was associated with simulta- neous initiation of cracks at the weld toe and inside the weld . As these cracks grew in widely offset planes their ...
... welds . == Effect of Weld Profile Stress Range - 150 MPa served in several joints , was associated with simulta- neous initiation of cracks at the weld toe and inside the weld . As these cracks grew in widely offset planes their ...
Page 442
... WELD TOE SURFACE CRACKS The tubular joint weld toe crack under fatigue loading tends to grow along the weld toe contour on the surface , in general . Along the tubular thickness direction , it usually propagates following a curved path ...
... WELD TOE SURFACE CRACKS The tubular joint weld toe crack under fatigue loading tends to grow along the weld toe contour on the surface , in general . Along the tubular thickness direction , it usually propagates following a curved path ...
Contents
THICKNESS EFFECT | 305 |
OFFSHORE TECHNOLOGY PART | 315 |
Influence of the Welding Procedure on the Ferrite Content and Fracture Toughness of Duplex | 323 |
Copyright | |
26 other sections not shown
Other editions - View all
Common terms and phrases
A36 steel as-welded joints assessment Basic behaviour bending brace calculated cathodic protection chord comparison composite computed corrosion fatigue crack depth crack front crack growth rate crack initiation crack length crack propagation crack tip cruciform joints defect diameter Dover failure fatigue crack growth fatigue life predictions fatigue strength fatigue test Figure finite element finite element analysis fracture mechanics geometry impact improved increasing integration layer method Nominal Stress number of cycles Offshore Mechanics offshore structures OMAE parameters parametric equations performed plastic plate thickness procedure ratio residual stress root S-N curves saddle seawater short cracks shown SIF solutions specimens strain strain gauge strand stress concentration stress concentration factors stress distribution stress intensity factor stress range surface crack T-joints Table technique Tee joints temperature tendon tensile tension tubular joints values variable amplitude Volume III-B weight function weld profile weld toe Welded Joints weldments wire