Multicomponent Polymer Systems: Phase Behavior, Dynamics and Applications : November 29-December 3, 2004, Boston, Massachusetts, USA. |
From inside the book
Results 1-3 of 5
Page 21
... ( PMDA ) and Maleic Anhydride ( MA ) were used as potential chain extension / branching agents . The nanocomposites were prepared in two extrusion steps . In the first run , 3 % Cloisite 25A and 97 % R - PET containing nanocomposites were ...
... ( PMDA ) and Maleic Anhydride ( MA ) were used as potential chain extension / branching agents . The nanocomposites were prepared in two extrusion steps . In the first run , 3 % Cloisite 25A and 97 % R - PET containing nanocomposites were ...
Page 24
... PMDA APET - 3 % 25A - MA 500 0 0.25 0.5 0.75 1 1.25 MA - PMDA Content ( Weight % ) Young's Modulus ( MPa ) Figure 3. Effect of MA or PMDA content on Young's modulus of 3 weight % Cloisite25A containing nanocomposites . Effects of MA and ...
... PMDA APET - 3 % 25A - MA 500 0 0.25 0.5 0.75 1 1.25 MA - PMDA Content ( Weight % ) Young's Modulus ( MPa ) Figure 3. Effect of MA or PMDA content on Young's modulus of 3 weight % Cloisite25A containing nanocomposites . Effects of MA and ...
Page 25
... PMDA RPET - 3 % 25A - MA 1 1.25 MA - PMDA Content ( Weight % ) Figure 5. Effect of MA or PMDA content on tensile strain at break of 3 weight % Cloisite 25A containing nanocomposites As seen in Figure 5 , the tensile strain at break ...
... PMDA RPET - 3 % 25A - MA 1 1.25 MA - PMDA Content ( Weight % ) Figure 5. Effect of MA or PMDA content on tensile strain at break of 3 weight % Cloisite 25A containing nanocomposites As seen in Figure 5 , the tensile strain at break ...
Contents
Rich Dynamics in Diblock Copolymers | 1 |
On the Origin of Color Degradation in Polyfluorenes Block Copolymer | 14 |
Influence of the Particle Morphology on the MicroAnd Macromechanics | 30 |
Copyright | |
2 other sections not shown
Common terms and phrases
2005 Materials Research amorphous annealing behavior block copolymers chain Chem cluster co-continuous component composite electrodes conductivity counterion crystalline decrease diffusion dynamic mechanical analysis dynamics E-MA-GMA effect emission endothermic epoxide ESC resistance experimental extruded fiber length fibrous clay filler films flexural modulus fluid glass transition glass transition temperature HDPE homopolymer Im3m immiscible increases initiator intensity interactions interfacial ionomer irradiated layer liquid crystal Macromolecules Materials Research Society matrix measurements mechanical properties melt melt-blended composite membranes molecular weight monomers morphology Nafion nanocomposites nanoparticles nanorods NTDA-ODADS/ODA observed obtained P(VDF-TrFE parameters particles PCLD peak performance PFOS phase separation Phys platelet PMDA PMMA polarization polydisperse polyimide polyimide copolymers polymer blends polymerization polystyrene pore PS/PP Raman ratio room temperature samples SAXS shown in Figure shows simulation solvent spectra spheres strain structure surface SWNT TFPS(II TFPSF thermal volume fraction X-ray