Deformation and Fracture Mechanics of Engineering MaterialsThis Third Edition of the well-received engineering materials book has been completely updated, and now contains over 1,100 citations. Thorough enough to serve as a text, and up-to-date enough to serve as a reference. There is a new chapter on strengthening mechanisms in metals, new sections on composites and on superlattice dislocations, expanded treatment of cast and powder-produced conventional alloys, plastics, quantitative fractography, JIC and KIEAC test procedures, fatigue, and failure analysis. Includes examples and case histories. |
From inside the book
Results 1-3 of 53
Page 19
... curve , such as the one shown in Fig . 1.6 ; ( 2 ) construct a line parallel to the elastic portion of the σ - e curve but offset from the origin by a certain amount ( the ... deformation ( necking ) in the STRESS - STRAIN CURVES / 19.
... curve , such as the one shown in Fig . 1.6 ; ( 2 ) construct a line parallel to the elastic portion of the σ - e curve but offset from the origin by a certain amount ( the ... deformation ( necking ) in the STRESS - STRAIN CURVES / 19.
Page 25
... curve ( Fig . 1.5 ) after the onset of necking reflect the higher axial stresses necessitated by the triaxial stress con- dition . In terms of the radius of curvature of the neck contour R and the radius of ... STRESS - STRAIN CURVES / 25.
... curve ( Fig . 1.5 ) after the onset of necking reflect the higher axial stresses necessitated by the triaxial stress con- dition . In terms of the radius of curvature of the neck contour R and the radius of ... STRESS - STRAIN CURVES / 25.
Page 495
... stress - strain curve would be virtually coincident with the one generated by the locus of hysteresis loop tips . 55 By comparing monotonic and cyclically stabilized stress - strain curves , Landgraf et al . " demonstrated that certain ...
... stress - strain curve would be virtually coincident with the one generated by the locus of hysteresis loop tips . 55 By comparing monotonic and cyclically stabilized stress - strain curves , Landgraf et al . " demonstrated that certain ...
Contents
Tensile Response of Materials | 3 |
Elements of Dislocation Theory | 49 |
Slip and Twinning in Crystalline Solids | 81 |
Copyright | |
16 other sections not shown
Common terms and phrases
aluminum alloy applied stress associated ASTM ASTM STP atom behavior brittle Burgers vector ceramics Chapter Charpy component composite corrosion crack growth rate crack length crack tip craze creep crystal cycles cyclic da/dN decrease depends ductility elastic embrittlement engineering example failure fiber FIGURE flaw fracture mechanics fracture surface fracture toughness given grain boundaries hardening hydrogen increasing KIEAC Kmax ksivin lattice load martensite material matrix Mech metallurgical microstructure modulus MPaVm Note occur orientation particles phase plane-strain plastic deformation plastic zone plate polymer R. W. Hertzberg ratio region relation relative Reprinted with permission response result sample screw dislocation Section shear stress shown in Fig slip plane slip systems solid solution specimen stacking fault energy steel alloys strain rate stress concentration stress field stress intensity factor stress level stress-strain curve striation superalloys thickness Trans transition temperature twin values yield strength