Effect of Accelerated Weathering on the Physical and Mechanical Properties of Natural - Fiber Thermoplastic CompositesUniversity of Wisconsin--Madison, 2002 - 282 pages |
From inside the book
Results 1-3 of 40
Page viii
... 0.5 % Fungicide 39 22232 Table 3.3 Effects of Fungicide and Accelerated Weathering on Unfilled HDPE and PP resin 41 Table 3.4 Effects of Alternative Fibers and Accelerated Weathering on Total Color Difference for Thermoplastic Composites ...
... 0.5 % Fungicide 39 22232 Table 3.3 Effects of Fungicide and Accelerated Weathering on Unfilled HDPE and PP resin 41 Table 3.4 Effects of Alternative Fibers and Accelerated Weathering on Total Color Difference for Thermoplastic Composites ...
Page 46
... Composites with 0.5 % UV Stabilizer and 0.5 % Fungicide ( Mean values with error bars equal to one standard deviation ) 3.3.1.4 Effect of Fiber Type and Content Three different alternative fibers were investigated in this study , coir ...
... Composites with 0.5 % UV Stabilizer and 0.5 % Fungicide ( Mean values with error bars equal to one standard deviation ) 3.3.1.4 Effect of Fiber Type and Content Three different alternative fibers were investigated in this study , coir ...
Page 55
... composites with 0.5 % fungicide is 13 % greater than HDPE composites without fungicide . It is shown that the unexposed strength of PP composites with 2.0 % fungicide was 14 % less than composites without fungicide . The exposed ...
... composites with 0.5 % fungicide is 13 % greater than HDPE composites without fungicide . It is shown that the unexposed strength of PP composites with 2.0 % fungicide was 14 % less than composites without fungicide . The exposed ...
Common terms and phrases
Accelerated Weathering Additives antioxidant ASTM Change in Flexural chromaticity chromophores Coefficient of Variation color change Color Difference AE compatibilizer Composites with 0.25 compression side crystallinity degraded layer Depth of Degradation due to accelerated Effect of Accelerated Effect of Fungicide Effect of UV error bars equal exposed surface Exposure Figure Flexural Modulus flexural properties flexural strength Fungicide Gijsman HDPE 70 HDPE composites HDPE specimens hours of exposure hydroperoxides impact strength injection molded jute Kenaf lignin lignocellulosic materials matrix maximum load mechanical properties modulus for Formulation natural fibers natural weathering orientation outdoor oxidation oxygen Phase photodegradation photooxidation polymer Predicted Flexural Rabek radicals reactions reduced result roof panels show the effects sisal specimens exposed Stabilizer and Accelerated standard deviation strain strength for Formulation stress Table temperature tension side Thermoplastic Composites Total Color Difference unexposed modulus unexposed strength UV stabilizer values with error Visible Depth wavelengths Weathering on Flexural Wood Flour Composites Wood Flour Content