Effect of Accelerated Weathering on the Physical and Mechanical Properties of Natural - Fiber Thermoplastic CompositesUniversity of Wisconsin--Madison, 2002 - 282 pages |
From inside the book
Results 1-3 of 22
Page x
... Wood Flour Left , Weathered Specimen ( 1500 hours ) ; Right , Unweathered Specimen Figure 3.5 Surface Crazing of ... Content and Accelerated Weathering on the Total Color Difference of Thermoplastic Composites 44 Figure 3.13 Effect of Wood ...
... Wood Flour Left , Weathered Specimen ( 1500 hours ) ; Right , Unweathered Specimen Figure 3.5 Surface Crazing of ... Content and Accelerated Weathering on the Total Color Difference of Thermoplastic Composites 44 Figure 3.13 Effect of Wood ...
Page 24
... content for wood flour PP composites ( Berger 1997 ) . The flexural modulus of 20 % PP composites was found to increase 200 % - 250 % when 60 % wood flour was added , depending on the type of flour used ( Berger 1997 ) . Razi found that ...
... content for wood flour PP composites ( Berger 1997 ) . The flexural modulus of 20 % PP composites was found to increase 200 % - 250 % when 60 % wood flour was added , depending on the type of flour used ( Berger 1997 ) . Razi found that ...
Page 56
... Wood Flour - Thermoplastic Composites ( Mean values with error bars equal to one standard deviation ) 3.3.2.3 Effect of Wood Flour Content The effects of wood flour content and accelerated weathering on flexural properties were ...
... Wood Flour - Thermoplastic Composites ( Mean values with error bars equal to one standard deviation ) 3.3.2.3 Effect of Wood Flour Content The effects of wood flour content and accelerated weathering on flexural properties were ...
Common terms and phrases
Accelerated Weathering Additives antioxidant ASTM Change in Flexural chromaticity chromophores Coefficient of Variation color change Color Difference AE compatibilizer Composites with 0.25 compression side crystallinity degraded layer Depth of Degradation due to accelerated Effect of Accelerated Effect of Fungicide Effect of UV error bars equal exposed surface Exposure Figure Flexural Modulus flexural properties flexural strength Fungicide Gijsman HDPE 70 HDPE composites HDPE specimens hours of exposure hydroperoxides impact strength injection molded jute Kenaf lignin lignocellulosic materials matrix maximum load mechanical properties modulus for Formulation natural fibers natural weathering orientation outdoor oxidation oxygen Phase photodegradation photooxidation polymer Predicted Flexural Rabek radicals reactions reduced result roof panels show the effects sisal specimens exposed Stabilizer and Accelerated standard deviation strain strength for Formulation stress Table temperature tension side Thermoplastic Composites Total Color Difference unexposed modulus unexposed strength UV stabilizer values with error Visible Depth wavelengths Weathering on Flexural Wood Flour Composites Wood Flour Content