Glass, Volume 1Minoru Tomozawa, Robert H. Doremus |
From inside the book
Results 1-3 of 28
Page 162
... concentration of one component fluctuates away from the equilibrium value by ... concentration fluctuations becomes < ck * ( t ) · Cx ( t + T ) ) = < | Ac1 | 2 ) exp ( − Dk2 | t | ) ( 6 ) ... fluctuations to the variation of 162 JOHN SCHROEDER.
... concentration of one component fluctuates away from the equilibrium value by ... concentration fluctuations becomes < ck * ( t ) · Cx ( t + T ) ) = < | Ac1 | 2 ) exp ( − Dk2 | t | ) ( 6 ) ... fluctuations to the variation of 162 JOHN SCHROEDER.
Page 170
... concentration fluctuations of wave vector k , and in general Té Tr . Thus for a n - component system in general terms the Landau - Placzek ratio for concentration fluctuations becomes RLP ( C ) ΤΣ και n - 1 = ( dE / DCj ) T‚P , { c ́ } ...
... concentration fluctuations of wave vector k , and in general Té Tr . Thus for a n - component system in general terms the Landau - Placzek ratio for concentration fluctuations becomes RLP ( C ) ΤΣ και n - 1 = ( dE / DCj ) T‚P , { c ́ } ...
Page 185
... concentration fluctuations the broad background , attributable to density fluctuations , was calculated with the aid of Eq . ( 39 ) . High - temperature ultrasonic data ( Bockris et al . , 1955 ; Bockris and Kojonen , 1960 ; Bloom and ...
... concentration fluctuations the broad background , attributable to density fluctuations , was calculated with the aid of Eq . ( 39 ) . High - temperature ultrasonic data ( Bockris et al . , 1955 ; Bockris and Kojonen , 1960 ; Bloom and ...
Contents
Text | 8 |
Ultraviolet Absorption | 10 |
Visible Absorption | 35 |
Copyright | |
49 other sections not shown
Common terms and phrases
absorption alkali anisotropic annealing applications assumed atoms band birefringence bleaching bond Bray Brillouin calculations caused Ceram charge Chem coefficient color composition concentration considered constant containing coordination copper crystal crystalline curve darkening density dependence described detailed determined dielectric diffusion discussed distribution effect electron energy equilibrium et al experimental fading field Figure fluctuations frequency function given gives heat heat treatment hole increase indicated intensity ions levels light liquid material measured microstructural mole negative birefringence observed obtained optical oxide oxygen particles phase photochromic Phys polarization positive present produce range ratio reduced relaxation reported respectively sample scattering separation shift shown in Fig shows silicate glasses silver halide similar SiO2 sodium Solids spectra spectrum strain stress stretching structural studied Taylor techniques temperature term thermal tion transition trapped viscosity wavelengths York