... measured the absorption in soda - lime silicate and potash - lime - silica glasses containing Mn3 + and observed a single band in each at 0.47 and 0.52 μm , respectively . Turner and Weyl ( 1935 ) added arsenic and antimony ( reducing ...
... measured the absorption in soda - lime silicate and potash - lime - silica glasses containing Mn3 + and observed a single band in each at 0.47 and 0.52 μm , respectively . Turner and Weyl ( 1935 ) added arsenic and antimony ( reducing ...
Page 77
... measured the Raman spectra of a number of simple phos- phate glasses including P2O5 . The spectrum was characterized by peaks near 325 , 700 , 1150 , and 1360 cm1 . The strong bands near 700 and 1150 cm were attributed to the symmetric ...
... measured the Raman spectra of a number of simple phos- phate glasses including P2O5 . The spectrum was characterized by peaks near 325 , 700 , 1150 , and 1360 cm1 . The strong bands near 700 and 1150 cm were attributed to the symmetric ...
Page 198
... measured Brillouin intensity ratio and from the measured Brillouin splitting , respec- tively . Thus , the measured Landau - Placzek ratio , and the Brillouin intensity and splitting allows the calculation of the total scattering ...
... measured Brillouin intensity ratio and from the measured Brillouin splitting , respec- tively . Thus , the measured Landau - Placzek ratio , and the Brillouin intensity and splitting allows the calculation of the total scattering ...
Contents
Text | 8 |
Ultraviolet Absorption | 10 |
Visible Absorption | 35 |
Copyright | |
49 other sections not shown
Common terms and phrases
absorption alkali anisotropic annealing applications assumed atoms band birefringence bleaching bond Bray Brillouin calculations caused Ceram charge Chem coefficient color composition concentration considered constant containing coordination copper crystal crystalline curve darkening density dependence described detailed determined dielectric diffusion discussed distribution effect electron energy equilibrium et al experimental fading field Figure fluctuations frequency function given gives heat heat treatment hole increase indicated intensity ions levels light liquid material measured microstructural mole negative birefringence observed obtained optical oxide oxygen particles phase photochromic Phys polarization positive present produce range ratio reduced relaxation reported respectively sample scattering separation shift shown in Fig shows silicate glasses silver halide similar SiO2 sodium Solids spectra spectrum strain stress stretching structural studied Taylor techniques temperature term thermal tion transition trapped viscosity wavelengths York