Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 88
Page 139
minimum hardness value is located near the HAZ / base metal boundary . The width of softened zone is around 15 mm . As expected from the hardness distribution in Fig . 4 , a decrease of 68 MPa in tensile strength was observed .
minimum hardness value is located near the HAZ / base metal boundary . The width of softened zone is around 15 mm . As expected from the hardness distribution in Fig . 4 , a decrease of 68 MPa in tensile strength was observed .
Page 227
450r T O 3.30 Ni , 210 mm on the fusion line ( FL ) , and in the HAZ at 2 mm from the fusion line toward the base metal ( FL + 2 mm ) . The 2 mm V - notch Charpy impact test results of welded joints are shown in Table 7.
450r T O 3.30 Ni , 210 mm on the fusion line ( FL ) , and in the HAZ at 2 mm from the fusion line toward the base metal ( FL + 2 mm ) . The 2 mm V - notch Charpy impact test results of welded joints are shown in Table 7.
Page 216
1 ) sample disc , 2 ) L - base , 3 , 4 ) sample holder , 5 ) spacer . Disc 22.6 mm Dia . Test Surface Ice . Impact From Izod Hammer L - Base Spacer Vice using a mold and then welding the ice to the L - base , and 2 ) bonding both the ...
1 ) sample disc , 2 ) L - base , 3 , 4 ) sample holder , 5 ) spacer . Disc 22.6 mm Dia . Test Surface Ice . Impact From Izod Hammer L - Base Spacer Vice using a mold and then welding the ice to the L - base , and 2 ) bonding both the ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
Measurement and Prediction of Welding Residual Stresses Using | 7 |
WELD METAL AND HAZ PROPERTIES | 37 |
Copyright | |
48 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis application axial base bending calculated CGHAZ coating compared components composition connection considered constant cooling corrosion cost crack critical CTOD curves cycle depth developed distribution effect element energy Engineering evaluation experimental experiments factor fatigue field Figure fracture geometry given Grade grain hardness heat higher improved increase indicated initiation length living load lower material measured mechanical metal method microstructure notched observed obtained offshore operation parameters pass performed pipe plate position possible prediction present pressure procedure production properties range reduced region residual stress resistance root seawater shown shows simulation specimens steel strain strength structure surface Table technique temperature tensile thermal thickness Titanium toughness values weld metal welded joints wire yield zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1991 |
| Export Citation | BiBTeX EndNote RefMan |