Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 86
Page 81
... higher strength steels for any given application . Seven steels of between 15 and 50mm thickness were examined , made by a range of process routes . All steels were initially characterised in terms of strength , Charpy toughness ...
... higher strength steels for any given application . Seven steels of between 15 and 50mm thickness were examined , made by a range of process routes . All steels were initially characterised in terms of strength , Charpy toughness ...
Page 157
... higher pressure . Further experiments showed that controlled arc voltage amplitudes are increasing with higher coil currents and arc lengths , but decrease at higher frequencies , as also reported elsewhere ( 4 ) . Most significant ...
... higher pressure . Further experiments showed that controlled arc voltage amplitudes are increasing with higher coil currents and arc lengths , but decrease at higher frequencies , as also reported elsewhere ( 4 ) . Most significant ...
Page 612
... higher the surface area / volume ratio of the specimen was , showing effects of restrained deformation by the core of the specimens similar as observed for dry - shrinkage . This dependency of specimen size was more pronounced for ...
... higher the surface area / volume ratio of the specimen was , showing effects of restrained deformation by the core of the specimens similar as observed for dry - shrinkage . This dependency of specimen size was more pronounced for ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
Measurement and Prediction of Welding Residual Stresses Using | 7 |
Prediction of Residual Stresses and Distortions in Welded Structures | 25 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
aluminium amplitude analysis as-welded austenite axial bending calculated CGHAZ Charpy chemical composition coating components cooling corrosion crack front crack tip CTOD CTOD fracture toughness CTOD test CTOD value curves developed diameter distribution evaluation experimental factor fatigue crack fatigue strength ferrite Figure fracture mechanics fracture toughness gauges geometry Grade grain groove Gullfaks heat input ICCGHAZ increase kJ/mm living quarter load martensite Materials Engineering ASME measured mechanical properties method microstructure multi-pass narrow gap offshore structures OMAE parameters pearlite pipe plate thickness Pop-in prediction pressure PWHT residual stress riser S-N curves seawater shown simulation slot Statoil steel plate strain gauges stress concentration stress range surface notched Table tapered joint temperature tensile thickness effect titanium alloys TMCP tubular underwater welding weld metal weld toe welded joints Welding Institute welding procedure welding process welding residual stress weldments wire yield strength zone