Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 86
Page 352
170 IEO fatigue data , respectively , for the first of these ( TIG dressing ) , while Figure 9 presents fatigue strength versus Kt data for welds based upon improved electrodes ( 43 ) for welds of the geometries reported in Figure 10 .
170 IEO fatigue data , respectively , for the first of these ( TIG dressing ) , while Figure 9 presents fatigue strength versus Kt data for welds based upon improved electrodes ( 43 ) for welds of the geometries reported in Figure 10 .
Page 353
The former representation ( Figure 13 ) indicates enhanced fatigue life for the improved profile specimens ; however , the authors concluded from the latter ( Figure 14 ) that profiling per se had no effect other than to transpose the ...
The former representation ( Figure 13 ) indicates enhanced fatigue life for the improved profile specimens ; however , the authors concluded from the latter ( Figure 14 ) that profiling per se had no effect other than to transpose the ...
Page 563
The values are very similar to those listed above for conditioning at 710 and 95 % relative humidity . water was were to to room a Solvent Resistance Solvent resistance of improved PPS composites LG40-70 , LG31-60 , and LG20-40 in ...
The values are very similar to those listed above for conditioning at 710 and 95 % relative humidity . water was were to to room a Solvent Resistance Solvent resistance of improved PPS composites LG40-70 , LG31-60 , and LG20-40 in ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
Measurement and Prediction of Welding Residual Stresses Using | 7 |
WELD METAL AND HAZ PROPERTIES | 37 |
Copyright | |
48 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis application axial base bending calculated CGHAZ coating compared components composition connection considered constant cooling corrosion cost crack critical CTOD curves cycle depth developed distribution effect element energy Engineering evaluation experimental experiments factor fatigue field Figure fracture geometry given Grade grain hardness heat higher improved increase indicated initiation length living load lower material measured mechanical metal method microstructure notched observed obtained offshore operation parameters pass performed pipe plate position possible prediction present pressure procedure production properties range reduced region residual stress resistance root seawater shown shows simulation specimens steel strain strength structure surface Table technique temperature tensile thermal thickness Titanium toughness values weld metal welded joints wire yield zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1991 |
| Export Citation | BiBTeX EndNote RefMan |