Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 74
Page 521
... material fatigue properties and the stress intensity factor range AK , AONY✓na with Ao being the applied fatigue stress range . The material properties C and m are generally determined through a laboratory test in an environment ...
... material fatigue properties and the stress intensity factor range AK , AONY✓na with Ao being the applied fatigue stress range . The material properties C and m are generally determined through a laboratory test in an environment ...
Page 594
... material fabrication and installation costs . In other words , the total cost was reduced from NOK 5.2 mill . down to NOK 800 000 . Table 1 . Cost comparison from real case situations where the costs of carbon steel- and high molybdenum ...
... material fabrication and installation costs . In other words , the total cost was reduced from NOK 5.2 mill . down to NOK 800 000 . Table 1 . Cost comparison from real case situations where the costs of carbon steel- and high molybdenum ...
Page 616
... material selection criteria , followed by material investigation . Five different materials were selected and subjected to a series of tests , firstly to characterize their standard mechanical properties , then to assess their ...
... material selection criteria , followed by material investigation . Five different materials were selected and subjected to a series of tests , firstly to characterize their standard mechanical properties , then to assess their ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
Measurement and Prediction of Welding Residual Stresses Using | 7 |
Prediction of Residual Stresses and Distortions in Welded Structures | 25 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
aluminium amplitude analysis as-welded austenite axial bending calculated CGHAZ Charpy chemical composition coating components cooling corrosion crack front crack tip CTOD CTOD fracture toughness CTOD test CTOD value curves developed diameter distribution evaluation experimental factor fatigue crack fatigue strength ferrite Figure fracture mechanics fracture toughness gauges geometry Grade grain groove Gullfaks heat input ICCGHAZ increase kJ/mm living quarter load martensite Materials Engineering ASME measured mechanical properties method microstructure multi-pass narrow gap offshore structures OMAE parameters pearlite pipe plate thickness Pop-in prediction pressure PWHT residual stress riser S-N curves seawater shown simulation slot Statoil steel plate strain gauges stress concentration stress range surface notched Table tapered joint temperature tensile thickness effect titanium alloys TMCP tubular underwater welding weld metal weld toe welded joints Welding Institute welding procedure welding process welding residual stress weldments wire yield strength zone