Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5American Society of Mechanical Engineers, 1991 - Arctic regions |
From inside the book
Results 1-3 of 80
Page 84
stresses a a fusion boundary , the CTOD in the soft region was still high com = 0.57mm ) and the drop is unlikely to be important . In M5 , however , a & c value of 0.11mm was measured , compared with a minimum value of ou 0.28mm at the ...
stresses a a fusion boundary , the CTOD in the soft region was still high com = 0.57mm ) and the drop is unlikely to be important . In M5 , however , a & c value of 0.11mm was measured , compared with a minimum value of ou 0.28mm at the ...
Page 111
For the single - pass welds , the HAZ can be divided into four regions by the peak temperature To reached : i . ... When more than two passes are deposited , parts of HAZ region are followed by a tempering thermal cycle .
For the single - pass welds , the HAZ can be divided into four regions by the peak temperature To reached : i . ... When more than two passes are deposited , parts of HAZ region are followed by a tempering thermal cycle .
Page 268
Region 3 Region 2 Region M 5 mm ( a ) Test piece A 5 mm ca Test piece A Region 1 Region 2 , 5 mm ( b ) Test piece B Fig.12 C - scan images of flaw size and distribution 5 mm area attesi piene B Fig.11 Scanning graphs of squared region ...
Region 3 Region 2 Region M 5 mm ( a ) Test piece A 5 mm ca Test piece A Region 1 Region 2 , 5 mm ( b ) Test piece B Fig.12 C - scan images of flaw size and distribution 5 mm area attesi piene B Fig.11 Scanning graphs of squared region ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
Measurement and Prediction of Welding Residual Stresses Using | 7 |
WELD METAL AND HAZ PROPERTIES | 37 |
Copyright | |
48 other sections not shown
Other editions - View all
Common terms and phrases
alloys aluminium analysis application axial base bending calculated CGHAZ coating compared components composition connection considered constant cooling corrosion cost crack critical CTOD curves cycle depth developed distribution effect element energy Engineering evaluation experimental experiments factor fatigue field Figure fracture geometry given Grade grain hardness heat higher improved increase indicated initiation length living load lower material measured mechanical metal method microstructure notched observed obtained offshore operation parameters pass performed pipe plate position possible prediction present pressure procedure production properties range reduced region residual stress resistance root seawater shown shows simulation specimens steel strain strength structure surface Table technique temperature tensile thermal thickness Titanium toughness values weld metal welded joints wire yield zone
Bibliographic information
| Title | Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volumes 3-5 |
| Contributor | American Society of Mechanical Engineers. Offshore Mechanics and Arctic Engineering Division |
| Publisher | American Society of Mechanical Engineers, 1991 |
| Export Citation | BiBTeX EndNote RefMan |