... tempering strongly depends on the chemical composition . Figure 4 shows scanning electron microscopic views of ICCGHAZS tempered at several temperatures for steels NM and TM1 . Specimens were etched electrolytically through two ...
... tempering strongly depends on the chemical composition . Figure 4 shows scanning electron microscopic views of ICCGHAZS tempered at several temperatures for steels NM and TM1 . Specimens were etched electrolytically through two ...
Page 76
... tempered above 350 ° C . No recovery in toughness of the ICCGHAZ by tempering is expected for steel NM on the other ... tempered ICCGHAZS , and SCCGHAZs for steels TM1 and NM . where r is the distance from the fusion line , dHAZ is the ...
... tempered above 350 ° C . No recovery in toughness of the ICCGHAZ by tempering is expected for steel NM on the other ... tempered ICCGHAZS , and SCCGHAZs for steels TM1 and NM . where r is the distance from the fusion line , dHAZ is the ...
Page 112
... Tempered zone Tempered zone Tempered zone 1 Tempered zone 71 Plate thickness ( 50mm ) Tempered zone Tempered zone UACGHAZ Tempered ICCGHAZ zone MSCCGHAZ Tempered zone Tempered zone FGHAZ ICHAZ Frequency 9 ง -זזזז HT50 steel welds , T ...
... Tempered zone Tempered zone Tempered zone 1 Tempered zone 71 Plate thickness ( 50mm ) Tempered zone Tempered zone UACGHAZ Tempered ICCGHAZ zone MSCCGHAZ Tempered zone Tempered zone FGHAZ ICHAZ Frequency 9 ง -זזזז HT50 steel welds , T ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
Measurement and Prediction of Welding Residual Stresses Using | 7 |
Prediction of Residual Stresses and Distortions in Welded Structures | 25 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
aluminium amplitude analysis as-welded austenite axial bending calculated CGHAZ Charpy chemical composition coating components cooling corrosion crack front crack tip CTOD CTOD fracture toughness CTOD test CTOD value curves developed diameter distribution evaluation experimental factor fatigue crack fatigue strength ferrite Figure fracture mechanics fracture toughness gauges geometry Grade grain groove Gullfaks heat input ICCGHAZ increase kJ/mm living quarter load martensite Materials Engineering ASME measured mechanical properties method microstructure multi-pass narrow gap offshore structures OMAE parameters pearlite pipe plate thickness Pop-in prediction pressure PWHT residual stress riser S-N curves seawater shown simulation slot Statoil steel plate strain gauges stress concentration stress range surface notched Table tapered joint temperature tensile thickness effect titanium alloys TMCP tubular underwater welding weld metal weld toe welded joints Welding Institute welding procedure welding process welding residual stress weldments wire yield strength zone