... WELDED JOINTS The welded joint performance of the new steel was investigated by shielded metal arc welding ( SMAW ) and submerged arc welding ( SAW ) , two processes most frequently used for welding racks . The welding condi- tions are ...
... WELDED JOINTS The welded joint performance of the new steel was investigated by shielded metal arc welding ( SMAW ) and submerged arc welding ( SAW ) , two processes most frequently used for welding racks . The welding condi- tions are ...
Page 315
... welded steel joints with thicknesses ranging from 10 to 80mm . Cruciform joints and Tee joints with improved weld by overall profiling or toe- grinding were tested under pulsating tension and under pulsating bending , respectively ...
... welded steel joints with thicknesses ranging from 10 to 80mm . Cruciform joints and Tee joints with improved weld by overall profiling or toe- grinding were tested under pulsating tension and under pulsating bending , respectively ...
Page 317
... welded joints . The reduction of thickness effect in improved joints might be caused by the decreases not only in SCF , but also in the stress gradient around the toe . 4.2 Thickness Effect of Various Welded Joints The thickness effect ...
... welded joints . The reduction of thickness effect in improved joints might be caused by the decreases not only in SCF , but also in the stress gradient around the toe . 4.2 Thickness Effect of Various Welded Joints The thickness effect ...
Contents
RESIDUAL STRESS AND DISTORTION IN WELDS | 1 |
Measurement and Prediction of Welding Residual Stresses Using | 7 |
Prediction of Residual Stresses and Distortions in Welded Structures | 25 |
Copyright | |
56 other sections not shown
Other editions - View all
Common terms and phrases
aluminium amplitude analysis as-welded austenite axial bending calculated CGHAZ Charpy chemical composition coating components cooling corrosion crack front crack tip CTOD CTOD fracture toughness CTOD test CTOD value curves developed diameter distribution evaluation experimental factor fatigue crack fatigue strength ferrite Figure fracture mechanics fracture toughness gauges geometry Grade grain groove Gullfaks heat input ICCGHAZ increase kJ/mm living quarter load martensite Materials Engineering ASME measured mechanical properties method microstructure multi-pass narrow gap offshore structures OMAE parameters pearlite pipe plate thickness Pop-in prediction pressure PWHT residual stress riser S-N curves seawater shown simulation slot Statoil steel plate strain gauges stress concentration stress range surface notched Table tapered joint temperature tensile thickness effect titanium alloys TMCP tubular underwater welding weld metal weld toe welded joints Welding Institute welding procedure welding process welding residual stress weldments wire yield strength zone