## Treatise on Materials Science and Technology, Volume 4 |

### From inside the book

Results 1-3 of 37

Page 276

APPARENT

volume of loose powder . Naturally , the powder characteristics , size , shape ,

morphology , and internal porosity , affect the apparent

from 20 ...

APPARENT

**DENSITY**The apparent**density**corresponds to weight per unitvolume of loose powder . Naturally , the powder characteristics , size , shape ,

morphology , and internal porosity , affect the apparent

**density**, which can varyfrom 20 ...

Page 294

Typical results of Ep and

Therefore , the instantaneous value of the Poisson ratio can be obtained by

determining the ...

Typical results of Ep and

**density**vs. - E , are given in Fig . 30 . Because the**density**increases during compression , the Poisson ratio also increases .Therefore , the instantaneous value of the Poisson ratio can be obtained by

determining the ...

Page 295

The relation between Poisson ratio and

p is the

dense material . The exponent a in this relation is 1.92 for cold deformation ( Fig .

The relation between Poisson ratio and

**density**is given by y = 0.5p " ( 14 ) wherep is the

**density**of the porous material relative to theoretical**density**of the fullydense material . The exponent a in this relation is 1.92 for cold deformation ( Fig .

### What people are saying - Write a review

We haven't found any reviews in the usual places.

### Contents

RICHARD W VOOK | 2 |

Epitaxial Monocrystalline Films | 10 |

Polycrystalline Films | 37 |

Copyright | |

6 other sections not shown

### Other editions - View all

### Common terms and phrases

activity addition alloys applied approximation average beam becomes calculated compaction component composition compression concentration considered copper correlation corresponding crystal cubic curve decreases defined deformation density dependence determined diffraction diffusion direction discussed dislocation disorder distribution effect electron elements energy enthalpy entropy equations example experimental expression factor fault field Figure forged function given gives increases influence interaction jump lattice material measurements mechanism metal method neighbor observed obtained occurs oriented parameter partial pattern phases Phys plane polycrystalline position possible powder present probability production properties random ratio reflections region relative respectively shown in Fig shows single crystals sintered solid solution solute atoms solvent specimen strain strengthening stress structure Substituting surface Table temperature theoretical theory thermodynamic thin films tracer twin vacancy values variations volume X-ray yield