Page 116
Akhtar and Teghtsoonian ( 1969 ) have reported the dislocation density on the
basal plane of magnesium - aluminum single crystals increases with the square
root of the solute concentration . Hammar et al . conducted recent etch pit density
...
Akhtar and Teghtsoonian ( 1969 ) have reported the dislocation density on the
basal plane of magnesium - aluminum single crystals increases with the square
root of the solute concentration . Hammar et al . conducted recent etch pit density
...
Page 138
Critical resolved shear stress versus temperature for a series of copper -
aluminum alloy single crystals ( Koppenaal and Fine , 1962 ) . decreasing
temperature increases significantly with the aluminum content of copper single
crystals .
Critical resolved shear stress versus temperature for a series of copper -
aluminum alloy single crystals ( Koppenaal and Fine , 1962 ) . decreasing
temperature increases significantly with the aluminum content of copper single
crystals .
Page 141
This observation has since been reported for both single crystal ( Linde et al . ,
1950 ; Linde and Edwardson , 1954 ) ... Composition dependence of the critical
resolved shear stress for silver - gold single crystals ( Sachs and Weerts , 1930 ) .
This observation has since been reported for both single crystal ( Linde et al . ,
1950 ; Linde and Edwardson , 1954 ) ... Composition dependence of the critical
resolved shear stress for silver - gold single crystals ( Sachs and Weerts , 1930 ) .
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
RICHARD W VOOK | 2 |
Epitaxial Monocrystalline Films | 10 |
Polycrystalline Films | 37 |
Copyright | |
2 other sections not shown
Other editions - View all
Common terms and phrases
activity addition alloys applied approximation average beam becomes calculated compaction component composition compression concentration considered constant copper correlation corresponding crystal cubic curve decreases defined deformation density dependence determined diffraction diffusion direction discussed dislocation disorder distribution effect electron elements energy enthalpy entropy equations example experimental expression factor fault field Figure forged function given gives increases influence interaction jump lattice material measurements mechanism metal method neighbor observed obtained occurs oriented parameter partial pattern phases Phys plane polycrystalline position possible powder present probability production properties random ratio reflections region relative respectively shown in Fig shows single crystals sintered solid solution solute atoms solvent strain strengthening stress structure Substituting surface Table temperature theoretical theory thermodynamic thin films tracer twin vacancy values variations volume X-ray yield