Materials Selection for Process Plants |
From inside the book
Results 1-3 of 81
Page 77
... Table 8.6 . Ductile " Ni - Resist " Ductile nickel cast irons are produced by inoculating molten " Ni - Resist " with small amounts of magnesium . The magnesium treatment in the ladle converts the flake graphite of " Ni - Resist " to ...
... Table 8.6 . Ductile " Ni - Resist " Ductile nickel cast irons are produced by inoculating molten " Ni - Resist " with small amounts of magnesium . The magnesium treatment in the ladle converts the flake graphite of " Ni - Resist " to ...
Page 80
... Table 8.10 and its mechanical and physical properties in Table 8.11 . Whereas the thermal expansion of " Ni - Hard " is lower than that of the " Ni - Resists " , its density is greater . The hardness of these magnetic white irons is so ...
... Table 8.10 and its mechanical and physical properties in Table 8.11 . Whereas the thermal expansion of " Ni - Hard " is lower than that of the " Ni - Resists " , its density is greater . The hardness of these magnetic white irons is so ...
Page 111
... Table 10.1 where it can be compared to that of “ Durimet 20. " The similarity in analy- ses between " Worthite " and " Durimet 20 " results in similar physical and mechanical properties ; the properties of the cast alloy are given in Table ...
... Table 10.1 where it can be compared to that of “ Durimet 20. " The similarity in analy- ses between " Worthite " and " Durimet 20 " results in similar physical and mechanical properties ; the properties of the cast alloy are given in Table ...
Contents
American Cyanamid Co for providing the incentive to compile the data | 1 |
CATHODIC PROTECTION | 22 |
INHIBITORS | 28 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades gray iron handled hardened hardness Hastelloy heat heat-treatment hydrochloric acid Inconel increase lead machining Manganese material maximum mechanical properties metal surface Modulus of elasticity Monel natural rubber neoprene Ni-Resist nickel nitric acid paint phenolics physical and mechanical pipe plastic process industries rate of attack readily reducing Reduction of area resin room temperature rust salts sea water silicon solutions solvents stainless steels stress sulfuric acid tensile strength Tensile strength psi Thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium