Materials Selection for Process Plants |
From inside the book
Results 1-3 of 65
Page 65
... Annealed . 2 As - cast . Oil quenched and tempered . all welding should be done on fully annealed metal ; austenitic nickel - iron or carbon - steel rods may be used . The nickel - iron rods , generally , produce increased hardenability ...
... Annealed . 2 As - cast . Oil quenched and tempered . all welding should be done on fully annealed metal ; austenitic nickel - iron or carbon - steel rods may be used . The nickel - iron rods , generally , produce increased hardenability ...
Page 86
... annealed after welding . Furnace annealing is recommended . The welded part should be uniformly and slowly heated to 1400-1550 ° F , held for one hour per inch of thickness , but in any case not less than one - half hour , and then ...
... annealed after welding . Furnace annealing is recommended . The welded part should be uniformly and slowly heated to 1400-1550 ° F , held for one hour per inch of thickness , but in any case not less than one - half hour , and then ...
Page 149
... annealed cop- per was adopted by international agreement in 1913 , conductivity values are based on this standard . Todays commercial electrolytic coppers aver- age 101 per cent of International Annealed Copper Standard . When equal ...
... annealed cop- per was adopted by international agreement in 1913 , conductivity values are based on this standard . Todays commercial electrolytic coppers aver- age 101 per cent of International Annealed Copper Standard . When equal ...
Contents
American Cyanamid Co for providing the incentive to compile the data | 1 |
CATHODIC PROTECTION | 22 |
INHIBITORS | 28 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades gray iron handled hardened hardness Hastelloy heat heat-treatment hydrochloric acid Inconel increase lead machining Manganese material maximum mechanical properties metal surface Modulus of elasticity Monel natural rubber neoprene Ni-Resist nickel nitric acid paint phenolics physical and mechanical pipe plastic process industries rate of attack readily reducing Reduction of area resin room temperature rust salts sea water silicon solutions solvents stainless steels stress sulfuric acid tensile strength Tensile strength psi Thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium