Materials Selection for Process Plants |
From inside the book
Results 1-3 of 58
Page 15
... base metal , the stabilized electrodes will not prevent sensitization in the heat- affected zone of the unstabilized base metal . In such an instance , colum- bium does not diffuse from the weld area to the base metal . The extra - low ...
... base metal , the stabilized electrodes will not prevent sensitization in the heat- affected zone of the unstabilized base metal . In such an instance , colum- bium does not diffuse from the weld area to the base metal . The extra - low ...
Page 59
... base metal . Prior to welding , the part should be preheated to 600 ° F . After welding , the castings should be slowly cooled to room temperature . If properly made , the weld is normally as strong as the original casting and will be ...
... base metal . Prior to welding , the part should be preheated to 600 ° F . After welding , the castings should be slowly cooled to room temperature . If properly made , the weld is normally as strong as the original casting and will be ...
Page 168
... base metal . Wires produced for gas - welding are not suited for production of sound and pore - free inert - gas - shielded - arc welds . Either helium or argon can be used for inert gas shielding . Oxyacetylene welding offers the only ...
... base metal . Wires produced for gas - welding are not suited for production of sound and pore - free inert - gas - shielded - arc welds . Either helium or argon can be used for inert gas shielding . Oxyacetylene welding offers the only ...
Contents
American Cyanamid Co for providing the incentive to compile the data | 1 |
CATHODIC PROTECTION | 22 |
INHIBITORS | 28 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades gray iron handled hardened hardness Hastelloy heat heat-treatment hydrochloric acid Inconel increase lead machining Manganese material maximum mechanical properties metal surface Modulus of elasticity Monel natural rubber neoprene Ni-Resist nickel nitric acid paint phenolics physical and mechanical pipe plastic process industries rate of attack readily reducing Reduction of area resin room temperature rust salts sea water silicon solutions solvents stainless steels stress sulfuric acid tensile strength Tensile strength psi Thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium