Materials Selection for Process Plants |
From inside the book
Results 1-3 of 61
Page 62
... grades of pearlitic malleable iron are covered by ASTM specifica- tion A - 220 . An analysis of malleable iron is ... grades to 90,000 psi for the pearlitic grades . As the tensile strength increases , the elongation decreases . The in ...
... grades of pearlitic malleable iron are covered by ASTM specifica- tion A - 220 . An analysis of malleable iron is ... grades to 90,000 psi for the pearlitic grades . As the tensile strength increases , the elongation decreases . The in ...
Page 64
... grades of nodular iron . Grade 60-45-10 ( ferritic ) and Grade 80-60-03 ( pearlitic ) are general - purpose irons cov- ered in ASTM A - 339 . Pressure - vessel grade nodular irons for service at elevated temperature are specified as ...
... grades of nodular iron . Grade 60-45-10 ( ferritic ) and Grade 80-60-03 ( pearlitic ) are general - purpose irons cov- ered in ASTM A - 339 . Pressure - vessel grade nodular irons for service at elevated temperature are specified as ...
Page 89
... grades . The danger of cracking due to air - hardening is eliminated in the ferritic grades . Cold - working is also easily performed ; work - harden- ing is minimized . Ferritic steels , when heated to about 200-300 ° F , are more ...
... grades . The danger of cracking due to air - hardening is eliminated in the ferritic grades . Cold - working is also easily performed ; work - harden- ing is minimized . Ferritic steels , when heated to about 200-300 ° F , are more ...
Contents
American Cyanamid Co for providing the incentive to compile the data | 1 |
CATHODIC PROTECTION | 22 |
INHIBITORS | 28 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades gray iron handled hardened hardness Hastelloy heat heat-treatment hydrochloric acid Inconel increase lead machining Manganese material maximum mechanical properties metal surface Modulus of elasticity Monel natural rubber neoprene Ni-Resist nickel nitric acid paint phenolics physical and mechanical pipe plastic process industries rate of attack readily reducing Reduction of area resin room temperature rust salts sea water silicon solutions solvents stainless steels stress sulfuric acid tensile strength Tensile strength psi Thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium