Materials Selection for Process Plants |
From inside the book
Results 1-3 of 88
Page 168
... Nickel is relatively inactive . In the presence of common acids , nickel does not readily discharge hydrogen from the metal surface . For corrosion to proceed , a supply of some oxidizing agent , such as dissolved air , is neces- sary ...
... Nickel is relatively inactive . In the presence of common acids , nickel does not readily discharge hydrogen from the metal surface . For corrosion to proceed , a supply of some oxidizing agent , such as dissolved air , is neces- sary ...
Page 169
... nickel bleaching equipment . The effect of sulfuric acid is varied . Unaerated , cold sulfuric acid below 80 per cent concentration causes a minor loss of metal ; on the other hand , the hot acid is quite ... NICKEL AND NICKEL ALLOYS 169.
... nickel bleaching equipment . The effect of sulfuric acid is varied . Unaerated , cold sulfuric acid below 80 per cent concentration causes a minor loss of metal ; on the other hand , the hot acid is quite ... NICKEL AND NICKEL ALLOYS 169.
Page 175
... nickel - chromium - iron alloy . Its chemical composition as given in Table 14.2 is compared with other nickel alloys . The chromium and nickel make it superior to nickel for use in oxidizing conditions , while the high nickel content ...
... nickel - chromium - iron alloy . Its chemical composition as given in Table 14.2 is compared with other nickel alloys . The chromium and nickel make it superior to nickel for use in oxidizing conditions , while the high nickel content ...
Contents
American Cyanamid Co for providing the incentive to compile the data | 1 |
CATHODIC PROTECTION | 22 |
INHIBITORS | 28 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades gray iron handled hardened hardness Hastelloy heat heat-treatment hydrochloric acid Inconel increase lead machining Manganese material maximum mechanical properties metal surface Modulus of elasticity Monel natural rubber neoprene Ni-Resist nickel nitric acid paint phenolics physical and mechanical pipe plastic process industries rate of attack readily reducing Reduction of area resin room temperature rust salts sea water silicon solutions solvents stainless steels stress sulfuric acid tensile strength Tensile strength psi Thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium