Materials Selection for Process Plants |
From inside the book
Results 1-3 of 20
Page 213
... phenolics , furanes , polyesters , and epoxies . They can be compression , transfer , premix , and matched metal ... Phenolic Plastics The phenolic plastics were the first synthetic polymeric PLASTICS 213.
... phenolics , furanes , polyesters , and epoxies . They can be compression , transfer , premix , and matched metal ... Phenolic Plastics The phenolic plastics were the first synthetic polymeric PLASTICS 213.
Page 215
... Phenolics are both strong and light . The tensile strength ranges from 5,000-9,000 psi and the compressive strength from 11,000-15,000 psi . Large process vessels require external strapping or wood staves and hoops for additional ...
... Phenolics are both strong and light . The tensile strength ranges from 5,000-9,000 psi and the compressive strength from 11,000-15,000 psi . Large process vessels require external strapping or wood staves and hoops for additional ...
Page 272
... phenolics have been extensively used by industry . However , since the process groups are requiring better and better paints , the role of the phenolics has declined . The fair chemical resistance , poor color retention , and poor ...
... phenolics have been extensively used by industry . However , since the process groups are requiring better and better paints , the role of the phenolics has declined . The fair chemical resistance , poor color retention , and poor ...
Contents
American Cyanamid Co for providing the incentive to compile the data | 1 |
CATHODIC PROTECTION | 22 |
INHIBITORS | 28 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades gray iron handled hardened hardness Hastelloy heat heat-treatment hydrochloric acid Inconel increase lead machining Manganese material maximum mechanical properties metal surface Modulus of elasticity Monel natural rubber neoprene Ni-Resist nickel nitric acid paint phenolics physical and mechanical pipe plastic process industries rate of attack readily reducing Reduction of area resin room temperature rust salts sea water silicon solutions solvents stainless steels stress sulfuric acid tensile strength Tensile strength psi Thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium