Materials Selection for Process Plants |
From inside the book
Results 1-3 of 48
Page 25
... pipe in soil . For well - coated pipe , the cur- rent densities are about 1 per cent of those needed for bare pipe . As the coating deteriorates , the current demand increases and approaches that of bare pipe . The next step is to ...
... pipe in soil . For well - coated pipe , the cur- rent densities are about 1 per cent of those needed for bare pipe . As the coating deteriorates , the current demand increases and approaches that of bare pipe . The next step is to ...
Page 45
... pipe ends . Because standard and 4D wrought iron are red short in the temperature range of 1450-1750 ° F , they are forged at 2400 ° F and other hot - forming operations are performed at 1300 ° F . Man- ganese wrought iron is not red ...
... pipe ends . Because standard and 4D wrought iron are red short in the temperature range of 1450-1750 ° F , they are forged at 2400 ° F and other hot - forming operations are performed at 1300 ° F . Man- ganese wrought iron is not red ...
Page 231
... pipe and fittings . Normally , steel forms the casing for the pipe and cast iron for the fittings . Aluminum , stainless steel and other alloy backing materials are available on special order . This plastic - metal com- bination yields ...
... pipe and fittings . Normally , steel forms the casing for the pipe and cast iron for the fittings . Aluminum , stainless steel and other alloy backing materials are available on special order . This plastic - metal com- bination yields ...
Contents
American Cyanamid Co for providing the incentive to compile the data | 1 |
CATHODIC PROTECTION | 22 |
INHIBITORS | 28 |
Copyright | |
19 other sections not shown
Other editions - View all
Common terms and phrases
abrasion resistance alkalies aluminum aluminum alloys annealed anode applications austenitic austenitic stainless steels base metal brasses brazing Brinell bronzes carbide carbon steel cast iron cause cements cent chemical resistance chloride chromium coat coefficient of thermal cold-working compounds concentrations copper corrosion resistance cracking ductility effect elastomers electrodes elevated temperatures Elongation environments epoxies equipment exposure fabrication filler film furane grades gray iron handled hardened hardness Hastelloy heat heat-treatment hydrochloric acid Inconel increase lead machining Manganese material maximum mechanical properties metal surface Modulus of elasticity Monel natural rubber neoprene Ni-Resist nickel nitric acid paint phenolics physical and mechanical pipe plastic process industries rate of attack readily reducing Reduction of area resin room temperature rust salts sea water silicon solutions solvents stainless steels stress sulfuric acid tensile strength Tensile strength psi Thermal conductivity thermal expansion tion titanium Type welding wrought Yield strength Yield strength psi zinc zirconium