Materials Selection for Process Plants |
From inside the book
Results 1-3 of 41
Page 110
In sulfuric acid , alloy “ 20 ” has few equals among the conventional and
economical metals and alloys . Although in the range of 60 – 90 per cent acid
there is an acceleration in the rate of attack , alloy " 20 " provides satisfactory
resistance to ...
In sulfuric acid , alloy “ 20 ” has few equals among the conventional and
economical metals and alloys . Although in the range of 60 – 90 per cent acid
there is an acceleration in the rate of attack , alloy " 20 " provides satisfactory
resistance to ...
Page 131
Chlorimet 3 ” is not as resistant to reducing acids as “ Chlorimet 2 ' ' ; however , it
still has merit . ... The resistance to sulfuric acid is excellent up to 40 per cent at
175°F and up to 10 per cent at the boiling point ; in sulfuric acid , however , this ...
Chlorimet 3 ” is not as resistant to reducing acids as “ Chlorimet 2 ' ' ; however , it
still has merit . ... The resistance to sulfuric acid is excellent up to 40 per cent at
175°F and up to 10 per cent at the boiling point ; in sulfuric acid , however , this ...
Page 169
The effect of sulfuric acid is varied . Unaerated , cold sulfuric acid below 80 per
cent concentration causes a minor loss of metal ; on the other hand , the hot acid
is quite corrosive . The intermediate ranges of sulfuric acid promote varying ...
The effect of sulfuric acid is varied . Unaerated , cold sulfuric acid below 80 per
cent concentration causes a minor loss of metal ; on the other hand , the hot acid
is quite corrosive . The intermediate ranges of sulfuric acid promote varying ...
What people are saying - Write a review
We haven't found any reviews in the usual places.
Contents
INTRODUCTION | 1 |
CATHODIC PROTECTION | 23 |
IRON AND STEEL | 44 |
Copyright | |
4 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acid addition alkalies alloys aluminum annealed anode applications atmospheres attack austenitic base brasses carbon carbon steel cast iron cause cements cent characteristics chemical resistance chloride cleaning coat combination common COMPANY compounds concentrations conductivity construction containing continuous cooling copper corrosion corrosion resistance cost cracking ductility effect electrical elevated Elongation environments equipment excellent exposure fabrication film given grades gray greater handled hardness heat heat-treatment improved increase industries lead limited lining lower machining material maximum mechanical properties metal method Monel natural nickel nitric normally occurs operating organic oxidizing paint performed physical pipe plastic prevent protection range readily recommended reducing removed rubber salts silicon sodium hypochlorite solutions solvents stainless steels stress structure suitable sulfuric acid superior surface Table temperature tensile strength thermal thickness tion titanium Type Typical welding widely wrought zinc