Mechanical MetallurgyI Mechanical Fundamentals 1 Introduction 2 Stress and Strain Relationships for Elastic Behavior 3 Elements of the Theory of Plasticity II Metallurgical Fundamentals 4 Plastic Deformation of Single Crystals 5 Dislocation Theory 6 Strengthening Mechanisms 7 Fracture III Applications to Materials Testing 8 The Tension Test 9 The Hardness Test 10 The Torsion Test 11 Fracture Mechanics 12 Fatigue of Metals 13 Creep and Stress Rupture 14 Brittle Fracture and Impact Testing IV Plastic Forming of Metals 15 Fundamentals of Metalworking 16 Forging 17 Rolling of Metals 18 Extrusion 19 Drawing of Rods, Wires and Tubes 20 Sheet-Metal Forming 21 Maching of Metals Appendixes |
From inside the book
Results 1-3 of 23
Page 221
... fiber - strengthened and dispersion- strengthened metals is that in fiber strengthening the high modulus fibers carry essentially all of the load . The matrix serves to transmit the load to the fibers , to protect fibers from surface ...
... fiber - strengthened and dispersion- strengthened metals is that in fiber strengthening the high modulus fibers carry essentially all of the load . The matrix serves to transmit the load to the fibers , to protect fibers from surface ...
Page 223
... fiber and on is the flow stress in the matrix at a strain equal to the fiber breaking stress . To obtain any benefit from the presence of fibers , the strength of the composite must be greater than the strength of the strain - hardened ...
... fiber and on is the flow stress in the matrix at a strain equal to the fiber breaking stress . To obtain any benefit from the presence of fibers , the strength of the composite must be greater than the strength of the strain - hardened ...
Page 224
... fiber Figure 6-24 Theoretical variation of composite strength with volume fraction of fiber ( for reinforcement with continuous fibers ) . The relationships between composite strength and volume fraction of fibers and the positions of ...
... fiber Figure 6-24 Theoretical variation of composite strength with volume fraction of fiber ( for reinforcement with continuous fibers ) . The relationships between composite strength and volume fraction of fibers and the positions of ...
Contents
Introduction | 3 |
Stress and Strain Relationships for Elastic Behavior | 18 |
Metallurgical Fundamentals | 101 |
Copyright | |
16 other sections not shown
Other editions - View all
Common terms and phrases
alloy aluminum angle annealed ASME ASTM atoms axis behavior billet brittle fracture Burgers vector cold-worked components compression constant crack creep cycles decrease determined diameter direction dislocation line ductile edge dislocation elastic elongation embrittlement energy engineering equation extrusion factor failure fatigue limit fibers Figure flow curve flow stress force forging friction given grain boundaries hot-working hydrostatic increase indentation lattice length load machining martensite material matrix maximum measured mechanical metallurgical Metals Park modulus necking notch occurs particles percent plane-strain plastic deformation plastic strain pressure produce properties ratio recrystallization reduction region residual stresses rolling screw dislocation shear stress sheet shown in Fig slip plane slip systems Society for Metals specimen steel strain hardening strain rate stress-strain curve structure surface temperature tensile strength tensile stress tension test tensor thickness tool torsion Trans usually velocity workpiece yield strength yield stress