Handbook of Plastics Technologies: The Complete Guide to Properties and PerformanceUnderstand, design, and manufacture plastics This resource provides you with the state-of-the-art information for the design, manufacture and application of plastics as well as its cutting-edge usage in nanotechnology.
|
From inside the book
Results 1-3 of 83
Page 3-14
... Impact-Strength Phenolics Notched Izod impact strength, fpi Filler None Wood flour Fabric Cord 0.25 0.3 2.4 7.0 TABLE 3.11 Effect of Fiber Length on Phenolic Impact Strength Fiber Notched Izod impact strength, fpi Ramie fiber, 1 in 1.0 ...
... Impact-Strength Phenolics Notched Izod impact strength, fpi Filler None Wood flour Fabric Cord 0.25 0.3 2.4 7.0 TABLE 3.11 Effect of Fiber Length on Phenolic Impact Strength Fiber Notched Izod impact strength, fpi Ramie fiber, 1 in 1.0 ...
Page 5-24
... strength to 70,000 psi Impact strength to 10 fpi HDT to 600°F Modulus to 3,000,000 psi Flexural strength to 80,000 psi Impact strength to 30 fpi HDT to 500°F TABLE 5.20 Impact Strength of Reinforced Nylon 6,6 Fiber length, inches fpi ...
... strength to 70,000 psi Impact strength to 10 fpi HDT to 600°F Modulus to 3,000,000 psi Flexural strength to 80,000 psi Impact strength to 30 fpi HDT to 500°F TABLE 5.20 Impact Strength of Reinforced Nylon 6,6 Fiber length, inches fpi ...
Page 5-58
... impact strength. It is grafted with maleic anhydride (maleated) and then grafted onto nylon to increase its impact strength. Recent news releases suggest that this technique is also being applied to other engineering thermoplastics ...
... impact strength. It is grafted with maleic anhydride (maleated) and then grafted onto nylon to increase its impact strength. Recent news releases suggest that this technique is also being applied to other engineering thermoplastics ...
Contents
Chapter 1 Introduction to Polymers and Plastics | 1-1 |
Chapter 2 Thermoplastics | 2-1 |
Chapter 3 Thermosets | 3-1 |
Copyright | |
7 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acetate acid acrylic addition adhesive agents applications automotive biodegradable blends blow molding bonding Brydson Butterworth-Heinemann carbon cellulose chain chemical chlorine coatings color composites compounds compression containers copolymers cross-linking crystalline cure degradation elastomers electrical electronics epoxy esters extrusion fasteners fibers FIGURE fillers film foam glass grades HDPE heat heat deflection temperature impact strength increase injection molding joint kpsi layers LDPE lubricant manufacturers mechanical melt metal modulus molecular weight molecules monomer nanocomposites nylon Oxford oxide packaging particles percent peroxide phenolic Plastics Engineering Handbook Plastics Industry Plastics Materials poly polycarbonate polyester polyethylene polyimides Polymer Science polymerization polypropylene polystyrene polysulfone polyurethane programs properties reaction recycling rate reinforcing resin resistance rubber screw silicate silicone solvent stability stress structure styrene sulfur surface TABLE Technology temperature tensile strength thermal thermoplastic thermoset thermoset plastics tion TPEs types typically vinyl viscosity vulcanizates vulcanization welding York