Handbook of Plastics Technologies: The Complete Guide to Properties and PerformanceUnderstand, design, and manufacture plastics This resource provides you with the state-of-the-art information for the design, manufacture and application of plastics as well as its cutting-edge usage in nanotechnology.
|
From inside the book
Results 1-3 of 34
Page 7-52
... welding . In hot gas welding , the weld joint is filled with a partially or fully molten polymer . This process is often used for long bond lines and for outdoor appli- cations where it is difficult to control conditions . Common ...
... welding . In hot gas welding , the weld joint is filled with a partially or fully molten polymer . This process is often used for long bond lines and for outdoor appli- cations where it is difficult to control conditions . Common ...
Page 7-53
... welding can be adapted to standard shop machinery such as drill presses or lathes. In commercial spin welding machines, rotational speeds can range from 200 to 14,000 rpm. Welding times (heating and cooling) can range from less than 1 ...
... welding can be adapted to standard shop machinery such as drill presses or lathes. In commercial spin welding machines, rotational speeds can range from 200 to 14,000 rpm. Welding times (heating and cooling) can range from less than 1 ...
Page 7-54
... welding are the joint design and induction coil design. With automatic equipment, welds can be made in less than 1 s. 7.5.1.5 Ultrasonic and Vibration Welding. Ultrasonic welding is a well accepted method for joining high-volume ...
... welding are the joint design and induction coil design. With automatic equipment, welds can be made in less than 1 s. 7.5.1.5 Ultrasonic and Vibration Welding. Ultrasonic welding is a well accepted method for joining high-volume ...
Contents
Chapter 1 Introduction to Polymers and Plastics | 1-1 |
Chapter 2 Thermoplastics | 2-1 |
Chapter 3 Thermosets | 3-1 |
Copyright | |
7 other sections not shown
Other editions - View all
Common terms and phrases
abrasion acetate acid acrylic addition adhesive agents applications automotive biodegradable blends blow molding bonding Brydson Butterworth-Heinemann carbon cellulose chain chemical chlorine coatings color composites compounds compression containers copolymers cross-linking crystalline cure degradation elastomers electrical electronics epoxy esters extrusion fasteners fibers FIGURE fillers film foam glass grades HDPE heat heat deflection temperature impact strength increase injection molding joint kpsi layers LDPE lubricant manufacturers mechanical melt metal modulus molecular weight molecules monomer nanocomposites nylon Oxford oxide packaging particles percent peroxide phenolic Plastics Engineering Handbook Plastics Industry Plastics Materials poly polycarbonate polyester polyethylene polyimides Polymer Science polymerization polypropylene polystyrene polysulfone polyurethane programs properties reaction recycling rate reinforcing resin resistance rubber screw silicate silicone solvent stability stress structure styrene sulfur surface TABLE Technology temperature tensile strength thermal thermoplastic thermoset thermoset plastics tion TPEs types typically vinyl viscosity vulcanizates vulcanization welding York