Deformation and Fracture Mechanics of Engineering MaterialsUpdated to reflect recent developments in our understanding of deformation and fracture processes in structural materials. This completely revised reference includes new sections on isostress analysis, modulus of rupture, creep fracture micromechanicsms, and many more. |
From inside the book
Results 1-3 of 72
Page 702
... surface treatments , failure to take remedial actions ( such as baking a steel part after it has been cadmium ... fracture surface . Delaminations 702 CHAPTER 14 ANALYSES OF ENGINEERING FAILURES Macroscopic Fracture Surface Examination.
... surface treatments , failure to take remedial actions ( such as baking a steel part after it has been cadmium ... fracture surface . Delaminations 702 CHAPTER 14 ANALYSES OF ENGINEERING FAILURES Macroscopic Fracture Surface Examination.
Page 751
Richard W. Hertzberg. APPENDIX A FRACTURE SURFACE PRESERVATION , CLEANING AND REPLICATION TECHNIQUES , AND IMAGE INTERPRETATION A.1 FRACTURE SURFACE PRESERVATION The first step to be taken prior to a fractographic examination — whether ...
Richard W. Hertzberg. APPENDIX A FRACTURE SURFACE PRESERVATION , CLEANING AND REPLICATION TECHNIQUES , AND IMAGE INTERPRETATION A.1 FRACTURE SURFACE PRESERVATION The first step to be taken prior to a fractographic examination — whether ...
Page 752
... ( surface to be cleaned is cathode with inert anode of carbon or platinum to prevent electroplating on fracture surface ) 6. Chemical etch cleaning Matter Removed Loosely adhering particles Hard and viscous debris Oils , greases Preformed ...
... ( surface to be cleaned is cathode with inert anode of carbon or platinum to prevent electroplating on fracture surface ) 6. Chemical etch cleaning Matter Removed Loosely adhering particles Hard and viscous debris Oils , greases Preformed ...
Other editions - View all
Common terms and phrases
addition aluminum alloy applied stress associated ASTM ASTM STP atoms behavior brittle Burgers vector ceramics Chapter Charpy component composite corrosion crack extension crack growth rate crack length crack propagation crack tip creep crystal curve cycles cyclic da/dN decrease depends determined dislocation ductility elastic embrittlement energy engineering example failure fatigue crack fiber FIGURE flaw fracture mechanics fracture surface fracture toughness given grain boundaries hydrogen increasing initial KIEAC Kmax lattice load maraging steels martensite material matrix Metals microstructure modulus MPa√m notch Note occur orientation particles phase plane-strain plastic deformation plastic zone plate polymer R. W. Hertzberg region Reprinted with permission result sample screw dislocation Section shear stress shown in Fig solid specimen stacking fault energy steel alloys stress concentration stress corrosion cracking stress intensity factor stress level stress-strain stress-strain curve test temperature thermal thickness toughening Trans transition temperature twin yield strength