Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 85
Page 376
... Table 1 and Table 2. respectively . Specimens The shape and size of a specimen in this study is shown in Fig . 1 with the detall configuration at notch and side groove . The specimen was named " new arrest specimen " . In this specimen ...
... Table 1 and Table 2. respectively . Specimens The shape and size of a specimen in this study is shown in Fig . 1 with the detall configuration at notch and side groove . The specimen was named " new arrest specimen " . In this specimen ...
Page 394
... Table 1 . Mechanical properties and chemical composition of real multi - pass weld joints are presented in Table 2 . WM mechanical properties were determined by round tensile specimens extracted from the root and the cap passes of X ...
... Table 1 . Mechanical properties and chemical composition of real multi - pass weld joints are presented in Table 2 . WM mechanical properties were determined by round tensile specimens extracted from the root and the cap passes of X ...
Page 497
... Table 10 , which shows chord crack depth varying from 6 % to 100 % of the wall thickness at N , ( INT ) . The remaining chord ligaments as a percentage of brace footprint area ( the shaded areas in Figure 2 ) are given in Table 11. At N ...
... Table 10 , which shows chord crack depth varying from 6 % to 100 % of the wall thickness at N , ( INT ) . The remaining chord ligaments as a percentage of brace footprint area ( the shaded areas in Figure 2 ) are given in Table 11. At N ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses ring riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength