Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 74
Page 412
... amount of cold - rolling , they remained at moderate level ( 20 % ) for 50 % cold - rolled steel at -196 ° C , and they were equal to or greater than the room temperature values when the amount of cold - rolling was 200 0 0 5 10 ARm ...
... amount of cold - rolling , they remained at moderate level ( 20 % ) for 50 % cold - rolled steel at -196 ° C , and they were equal to or greater than the room temperature values when the amount of cold - rolling was 200 0 0 5 10 ARm ...
Page 413
... Amount of cold - rolling , % Reduction of area , % Impact toughness , J 275 Specimen thickness : -20 ° C 250 7,5 mm ( 0-50 % cold - rolled ) -X --- 100 ° C 225 200 5 mm ( 70 % cold - rolled ) ᄆ A - 135 ° C -196 ° C 175 150 125 100 75 A ...
... Amount of cold - rolling , % Reduction of area , % Impact toughness , J 275 Specimen thickness : -20 ° C 250 7,5 mm ( 0-50 % cold - rolled ) -X --- 100 ° C 225 200 5 mm ( 70 % cold - rolled ) ᄆ A - 135 ° C -196 ° C 175 150 125 100 75 A ...
Page 414
... Amount of cold - rolling , % FIGURE 6. a ' - MARTENSITE CONTENT OF AISI 304LN STEEL AS A FUNCTION OF COLD - ROLLING MEASURED AT ROOM TEMPERATURE AND AFTER COOLING TO -196 AND -269 ° C . 0 10 20 30 40 50 60 70 Amount of cold - rolling ...
... Amount of cold - rolling , % FIGURE 6. a ' - MARTENSITE CONTENT OF AISI 304LN STEEL AS A FUNCTION OF COLD - ROLLING MEASURED AT ROOM TEMPERATURE AND AFTER COOLING TO -196 AND -269 ° C . 0 10 20 30 40 50 60 70 Amount of cold - rolling ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength