Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 74
Page 412
... Amount of cold - rolling , % 45 50 RESULTS Tensile tests 0 - 50 % cold - rolling of AISI 304LN steel increased yield strength gradually from 314 to 1005 MPa in room temperature tensile tests . The corresponding increase in tensile ...
... Amount of cold - rolling , % 45 50 RESULTS Tensile tests 0 - 50 % cold - rolling of AISI 304LN steel increased yield strength gradually from 314 to 1005 MPa in room temperature tensile tests . The corresponding increase in tensile ...
Page 413
... amount of cold - rolling was smaller than 20 % . After that , the martensite content increased with increasing amount of cold- rolling until it peaked at a level of about 2,5 % when amount of cold - rolling was 40 % . When cold - rolled ...
... amount of cold - rolling was smaller than 20 % . After that , the martensite content increased with increasing amount of cold- rolling until it peaked at a level of about 2,5 % when amount of cold - rolling was 40 % . When cold - rolled ...
Page 414
... Amount of cold - rolling , % 70 Amount of cold - rolling , % FIGURE 6. a ' - MARTENSITE CONTENT OF AISI 304LN STEEL AS A FUNCTION OF COLD - ROLLING MEASURED AT ROOM TEMPERATURE AND AFTER COOLING TO -196 AND -269 ° C . FIGURE 8 ...
... Amount of cold - rolling , % 70 Amount of cold - rolling , % FIGURE 6. a ' - MARTENSITE CONTENT OF AISI 304LN STEEL AS A FUNCTION OF COLD - ROLLING MEASURED AT ROOM TEMPERATURE AND AFTER COOLING TO -196 AND -269 ° C . FIGURE 8 ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses ring riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength