Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 65
Page 189
... brittle crack was initiated in the starter plate and caused to propagate into the test plate . The test results were evaluated by judging whether or not the test plate could arrest the brittle crack . ( d ) Sheer strake model test Such ...
... brittle crack was initiated in the starter plate and caused to propagate into the test plate . The test results were evaluated by judging whether or not the test plate could arrest the brittle crack . ( d ) Sheer strake model test Such ...
Page 375
... brittle crack arrestability , the over - matching concept was introduced . The possibility of the deviation in brittle crack propagation along the weldment was considered by using over - matching joints to make the best use of the ...
... brittle crack arrestability , the over - matching concept was introduced . The possibility of the deviation in brittle crack propagation along the weldment was considered by using over - matching joints to make the best use of the ...
Page 380
... brittle crack could be deviated by the over - matching effect into the base steel and might be arrested in the base steel with the best use of high crack arrestability . In this section , the availability of the new concept is proved ...
... brittle crack could be deviated by the over - matching effect into the base steel and might be arrested in the base steel with the best use of high crack arrestability . In this section , the availability of the new concept is proved ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength