Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 29
Page 158
... Coating thickness 0.2 ~ 0.8 mm Spraying distance Spraying verocity No. of passes Current 600 A 65 V 45 p / min Voltage Ar gas flow H2 gas flow Coating 80Ni - 20Cr Ø 40 SS400 40 25 cm / min . 2 rounds by Robot 13 p / min Adhesion SS400 ...
... Coating thickness 0.2 ~ 0.8 mm Spraying distance Spraying verocity No. of passes Current 600 A 65 V 45 p / min Voltage Ar gas flow H2 gas flow Coating 80Ni - 20Cr Ø 40 SS400 40 25 cm / min . 2 rounds by Robot 13 p / min Adhesion SS400 ...
Page 159
... Coating thickness , t ( mm ) Fig . 4 Effect of coating thickness on fracture load ( JIS - H8664 test ) . A ; Adhesion B ; Blasting C ; Coating Fig . 3 Fracture surface of tensile test specimen . relationship between the fracture load P ...
... Coating thickness , t ( mm ) Fig . 4 Effect of coating thickness on fracture load ( JIS - H8664 test ) . A ; Adhesion B ; Blasting C ; Coating Fig . 3 Fracture surface of tensile test specimen . relationship between the fracture load P ...
Page 163
... Coating thickness , t ( mm ) Fig . 14 Critical stress singularity parameter . Fig . 15 Small volume containing circular planar micro cracks under a triaxial stress state . vicinity of the coating / substrate interface and the coating ...
... Coating thickness , t ( mm ) Fig . 14 Critical stress singularity parameter . Fig . 15 Small volume containing circular planar micro cracks under a triaxial stress state . vicinity of the coating / substrate interface and the coating ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength