Page 412
... COLD - ROLLED AISI 304LN STEEL . 110 X. Strength , MPa 2000 1800 1600 1400 ... rolling of AISI 304LN steel increased yield strength gradually from 314 to ... cold - rolling ( Fig . 4 ) . When tensile tests were performed at -196 ° C ...
... COLD - ROLLED AISI 304LN STEEL . 110 X. Strength , MPa 2000 1800 1600 1400 ... rolling of AISI 304LN steel increased yield strength gradually from 314 to ... cold - rolling ( Fig . 4 ) . When tensile tests were performed at -196 ° C ...
Page 413
... cold - rolling , % Reduction of area , % Impact toughness , J 275 Specimen thickness : -20 ° C 250 7,5 mm ( 0-50 % cold - rolled ) -X --- 100 ° C 225 200 5 mm ( 70 % cold - rolled ) ᄆ A - 135 ° C -196 ° C 175 150 125 100 75 A ♡ 50 A ...
... cold - rolling , % Reduction of area , % Impact toughness , J 275 Specimen thickness : -20 ° C 250 7,5 mm ( 0-50 % cold - rolled ) -X --- 100 ° C 225 200 5 mm ( 70 % cold - rolled ) ᄆ A - 135 ° C -196 ° C 175 150 125 100 75 A ♡ 50 A ...
Page 415
... cold - rolling , % FIGURE 10. FORMATION OF a ' - MARTENSITE DURING CHARPY - V IMPACT TOUGHNESS TEST AT -196 ° C IN O - 70 % COLD - ROLLED AISI 304LN STEEL TOGETHER WITH CORRESPONDING IMPACT TOUGHNESS VALUES ( CVN ) . 1960 FSC HELSINK ...
... cold - rolling , % FIGURE 10. FORMATION OF a ' - MARTENSITE DURING CHARPY - V IMPACT TOUGHNESS TEST AT -196 ° C IN O - 70 % COLD - ROLLED AISI 304LN STEEL TOGETHER WITH CORRESPONDING IMPACT TOUGHNESS VALUES ( CVN ) . 1960 FSC HELSINK ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength