Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 43
Page 345
... crack propagation rates in structural steel " , UKOSRP report 3/03 , U.K. Dept. of Energy , 1975 5. R. Johnson and I Bretherton , " Fatigue data on constant amplitude tests on BS4360 : 50D steel in air and sea- water " , UKOSRP report 3 ...
... crack propagation rates in structural steel " , UKOSRP report 3/03 , U.K. Dept. of Energy , 1975 5. R. Johnson and I Bretherton , " Fatigue data on constant amplitude tests on BS4360 : 50D steel in air and sea- water " , UKOSRP report 3 ...
Page 451
... crack growth rates to be increased by a factor of 10 compared with those observed in - air . The results suggest that welding under controlled conditions does not significantly affect fatigue crack propagation in these steels , with ...
... crack growth rates to be increased by a factor of 10 compared with those observed in - air . The results suggest that welding under controlled conditions does not significantly affect fatigue crack propagation in these steels , with ...
Page 454
... crack growth rates indicate comparable behaviour to that observed for the parent plate . It would appear that welding under controlled conditions . does not significantly affect fatigue crack propagation in these steels and the data ...
... crack growth rates indicate comparable behaviour to that observed for the parent plate . It would appear that welding under controlled conditions . does not significantly affect fatigue crack propagation in these steels and the data ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength