Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 78
Page 215
... curves either by estimating the plateau load [ 11 ] or using the value of load on the load - displacement curve for the cracked joint corresponding to twice the linear elastic compliance of the uncracked joint [ 13 ] . the critical ...
... curves either by estimating the plateau load [ 11 ] or using the value of load on the load - displacement curve for the cracked joint corresponding to twice the linear elastic compliance of the uncracked joint [ 13 ] . the critical ...
Page 365
... curves are actually affected by various factors . The effect of strength mis - match on stable crack growth resistance is discussed in this paper . In order to compare the R curve of bi - material specimens with that of homogeneous ones ...
... curves are actually affected by various factors . The effect of strength mis - match on stable crack growth resistance is discussed in this paper . In order to compare the R curve of bi - material specimens with that of homogeneous ones ...
Page 441
load - displacement curve for axially loaded joints and from the moment - rotation curves for moment loaded joints . Whilst the curves for the uncracked joints showed a maximum ( or peak ) load , the load - displacement curves for the ...
load - displacement curve for axially loaded joints and from the moment - rotation curves for moment loaded joints . Whilst the curves for the uncracked joints showed a maximum ( or peak ) load , the load - displacement curves for the ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength