... Test data The data obtained from fatigue tests at h / s > 0.04 have provided evidence that there is an increasing reduction in fatigue performance as the shear key density ( h / s ) increases . However , owing to the small individual ...
... Test data The data obtained from fatigue tests at h / s > 0.04 have provided evidence that there is an increasing reduction in fatigue performance as the shear key density ( h / s ) increases . However , owing to the small individual ...
Page 473
... Fatigue tests carried out on ring stiffened tubular joints , of the kind widely used for the construction of offshore jacket structures , had indicated that fatigue cracks may occur in areas other than at external weld toes . The ...
... Fatigue tests carried out on ring stiffened tubular joints , of the kind widely used for the construction of offshore jacket structures , had indicated that fatigue cracks may occur in areas other than at external weld toes . The ...
Page 505
FATIGUE PERFORMANCE OF WELDED ALUMINUM DECK STRUCTURES Per J. Haagensen Department of Civil Engineering The ... tests on full scale sections of welded extrusions in the same material , which were used in an aluminum bridge deck structure .
FATIGUE PERFORMANCE OF WELDED ALUMINUM DECK STRUCTURES Per J. Haagensen Department of Civil Engineering The ... tests on full scale sections of welded extrusions in the same material , which were used in an aluminum bridge deck structure .
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength