Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 66
Page 235
... inspected by the original methods . INSPECTION DATA Defect Classification This paper considers the reportable and repairable defects which were detected and sized during fabrication inspections . In order to make an evaluation of the ...
... inspected by the original methods . INSPECTION DATA Defect Classification This paper considers the reportable and repairable defects which were detected and sized during fabrication inspections . In order to make an evaluation of the ...
Page 236
... inspected percentage of defects expressed as number of defective joints to total number of joints inspected . This information is presented for each structure , for each inspection method , for each joint type , and for reportable and ...
... inspected percentage of defects expressed as number of defective joints to total number of joints inspected . This information is presented for each structure , for each inspection method , for each joint type , and for reportable and ...
Page 240
PRE - REPAIR WELD INSPECTION RESULTS COMPLETE STRUCTURE JOINT TYPE INSPECTION METHOD DEFECT TYPE LENGTH INSPECTED ( m ) NO OF WELDS LENGTH DEFECTIVE % OF INSPECTED WELDS WITH DEFECTS اله reportable repairable all reportable repairable ...
PRE - REPAIR WELD INSPECTION RESULTS COMPLETE STRUCTURE JOINT TYPE INSPECTION METHOD DEFECT TYPE LENGTH INSPECTED ( m ) NO OF WELDS LENGTH DEFECTIVE % OF INSPECTED WELDS WITH DEFECTS اله reportable repairable all reportable repairable ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength