Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 79
Page 136
... LENGTH In TIG arcs the distance between tungsten electrode and workpiece is used as arc length . The maximum length of the plasma is normally longer , because it encloses part of a conical electrode tip . This additional length is ...
... LENGTH In TIG arcs the distance between tungsten electrode and workpiece is used as arc length . The maximum length of the plasma is normally longer , because it encloses part of a conical electrode tip . This additional length is ...
Page 237
... length and defective number of welds containing repairable defects than joint type B in Structure A from ultrasonic ... Length The mean length of repairable defects in Structure A was less than in Structure B. The mean length of ...
... length and defective number of welds containing repairable defects than joint type B in Structure A from ultrasonic ... Length The mean length of repairable defects in Structure A was less than in Structure B. The mean length of ...
Page 240
... LENGTH INSPECTED ( m ) NO OF WELDS LENGTH DEFECTIVE % OF INSPECTED WELDS WITH DEFECTS all reportable repairable all reportable repairable all MPI all 3697.1 1086 0.0 0.0 0.0 00 0.0 0.0 all UT all 3697.1 1086 1.36 0.30 1.06 25.0 15.2 ...
... LENGTH INSPECTED ( m ) NO OF WELDS LENGTH DEFECTIVE % OF INSPECTED WELDS WITH DEFECTS all reportable repairable all reportable repairable all MPI all 3697.1 1086 0.0 0.0 0.0 00 0.0 0.0 all UT all 3697.1 1086 1.36 0.30 1.06 25.0 15.2 ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses ring riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength