... pipe is in the dry condition approximately one to three minutes during an actual hydrocarbon fire . Preliminary testing shows that composite pipe is able to withstand this exposure to fire for the five minute duration of the test . This ...
... pipe is in the dry condition approximately one to three minutes during an actual hydrocarbon fire . Preliminary testing shows that composite pipe is able to withstand this exposure to fire for the five minute duration of the test . This ...
Page 266
... pipe used in named essential services in the engine room and in some other areas of a ship dictates that a pipe withstand , for 60 minutes , a temperature ramp of 1100 ° C . This test does not require that a pipe joint be tested . The ...
... pipe used in named essential services in the engine room and in some other areas of a ship dictates that a pipe withstand , for 60 minutes , a temperature ramp of 1100 ° C . This test does not require that a pipe joint be tested . The ...
Page 267
... pipe passed fire test if the nitrogen pressure was maintained for the five minute duration of the test . Next , the pipe was allowed to cool for 30 minutes and then hydrotested to 150 psi ( 10 bar ) . Passed * Weepage Occurred The butt ...
... pipe passed fire test if the nitrogen pressure was maintained for the five minute duration of the test . Next , the pipe was allowed to cool for 30 minutes and then hydrotested to 150 psi ( 10 bar ) . Passed * Weepage Occurred The butt ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength