Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 84
Page 189
... plate duplex ESSO test The ultra wide - plate duplex ESSO test was conducted by simulating the behavior of a brittle crack initiated in the outer hull of the struck ship and propagating in the sheer strake of the struck ship . Specimens ...
... plate duplex ESSO test The ultra wide - plate duplex ESSO test was conducted by simulating the behavior of a brittle crack initiated in the outer hull of the struck ship and propagating in the sheer strake of the struck ship . Specimens ...
Page 190
... PLATES . caused to penetrate the test plate at the target temperature of -50 deg.C under the tensile stress of 355 MPa . The results of the ultra wide - plate duplex ESSO test are summarized in Table 4. The SUF steel can arrest the ...
... PLATES . caused to penetrate the test plate at the target temperature of -50 deg.C under the tensile stress of 355 MPa . The results of the ultra wide - plate duplex ESSO test are summarized in Table 4. The SUF steel can arrest the ...
Page 385
... shows CTOD vs. GLS curves for base metal wide plate and wide plates containing root notched unrepaired and repaired welds . The repaired wide plate exhibits significantly . lower CTOD than the wide plate without repair for the 385.
... shows CTOD vs. GLS curves for base metal wide plate and wide plates containing root notched unrepaired and repaired welds . The repaired wide plate exhibits significantly . lower CTOD than the wide plate without repair for the 385.
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength