Proceedings of the ... International Conference on Offshore Mechanics and Arctic Engineering, Volume 15, Part 3American Society of Mechanical Engineers, 1996 - Arctic regions |
From inside the book
Results 1-3 of 64
Page 215
... predictions based on the HSE characteristic equations is demonstrated in Figure 7 for joints with ẞ greater than 0.6 . Figure 7 illustrates the effect of introducing the Q , factor for high ẞ joints , i.e. ẞ > 0.6 , to allow for the ...
... predictions based on the HSE characteristic equations is demonstrated in Figure 7 for joints with ẞ greater than 0.6 . Figure 7 illustrates the effect of introducing the Q , factor for high ẞ joints , i.e. ẞ > 0.6 , to allow for the ...
Page 216
representative of the predictions for all of the axial , OPB and IPB load cases investigated . FAD predictions were based on both the collapse load from the FE analysis and the predicted strength . The curves based on the load from the ...
representative of the predictions for all of the axial , OPB and IPB load cases investigated . FAD predictions were based on both the collapse load from the FE analysis and the predicted strength . The curves based on the load from the ...
Page 387
... prediction turns to be conservative . By refining some formulae ( for FYM and NM ) more accurate , or at least clear conservative predictions may be achieved which is one subject of ongoing work . For the notch position in the HAZ quite ...
... prediction turns to be conservative . By refining some formulae ( for FYM and NM ) more accurate , or at least clear conservative predictions may be achieved which is one subject of ongoing work . For the notch position in the HAZ quite ...
Contents
CODES AND STANDARDS | 1 |
EFFECT OF WELDING PARAMETERS ON JOINT PROPERTIES | 35 |
UNDERWATER WELDING AND REPAIR | 85 |
Copyright | |
9 other sections not shown
Other editions - View all
Common terms and phrases
a'-martensite analysis applied as-welded assessment austenite Axial tension base metal behaviour bending brace brittle butt welds cathodic protection CFRC chord crack cold-rolling composition corrosion corrosion fatigue crack depth crack growth rates crack initiation crack tip cracked joints CTOD curve cycles defects effect electrode Engineering equations evaluation experimental failure fatigue crack growth fatigue tests ferrite Figure fracture mechanics fracture toughness geometry heat affected zone heat treatment high strength steels hydrogen increased inspection martensite material measured microstructure mis-match notch offshore structures parameters performance pipe predicted pressure procedure PWHT ratio reduced residual stresses riser root S-N curves saddle seawater shielding gas shown simulation specimens static strength stiffened joints stress intensity factor surface crack Table temperature tensile thickness titanium alloys tubular joints ultrasonic unstiffened values weld joint weld metal weld toe weldments wide plates yield strength